ο “βαθούλωμα” προκαλείται από την τοπική συρρίκνωση μετά τη σφράγιση της πύλης ή προκαλείται από την έλλειψη έγχυσης υλικού. Η κοιλότητα ή η μικροκοίληση στην επιφάνεια των χυτευμένων προϊόντων με έγχυση είναι ένα παλιό πρόβλημα στη διαδικασία χύτευσης με έγχυση.
Dents are generally caused by the increase of the shrinkage rate of plastic products caused by the increase of the wall thickness. They may appear near the external sharp corner or the sudden change of the wall thickness, such as the bulge, the back of the stiffener or the support, and sometimes in some uncommon parts. The root cause of the dent is the thermal expansion and cold shrinkage of the material, because the coefficient of thermal expansion of thermoplastic is quite high. The degree of expansion and shrinkage depends on many factors, among which the most important are the properties of plastics, the maximum and minimum temperature range and the packing pressure in the cavity. The size and shape of injection parts, cooling rate and uniformity are also influencing factors.
The amount of expansion and shrinkage in the molding process of plastic materials is related to the coefficient of thermal expansion of the processed plastics, which is called “molding shrinkage”. With the cooling shrinkage of the molding part, the close contact between the molding part and the cooling surface of the mold cavity is lost. Αυτή τη στιγμή, the cooling efficiency decreases. After the molding part continues to cool, the molding part shrinks continuously. The shrinkage depends on the comprehensive effect of various factors.
The sharp corner on the molding part cools the fastest and hardens earlier than other parts. The thick part near the center of the molding part is farthest from the cooling surface of the cavity and becomes the last part to release heat on the molding part. After the material at the corner solidifies, with the melt cooling near the center of the part, the molding part will continue to shrink. The plane between the sharp corners can only be cooled on one side, and its strength has no change The strength of the material at the sharp corner is high. The cooling shrinkage of the plastic material in the center of the part pulls the relatively weak surface between the partially cooled and the more cooled sharp corner inward. Με αυτόν τον τρόπο, a dent is produced on the surface of the injection molded part.
The existence of the dent indicates that the shrinkage of the molding is higher than that of the surrounding parts. If the shrinkage of the molded part is higher in one place than in another, the reason for the warpage of the molded part is analyzed. The residual stress in the mold will reduce the impact strength and temperature resistance of the molded parts. Σε ορισμένες περιπτώσεις, the dent can be avoided by adjusting the process conditions. Για παράδειγμα, in the packing process of a molded part, additional plastic material is injected into the mold cavity to compensate for molding shrinkage. Στις περισσότερες περιπτώσεις, the gate is much thinner than the other parts of the part. When the molding part is still very hot and continues to shrink, the small gate has been cured. After curing, the packing pressure has no effect on the molding part in the cavity.
The results show that the shrinkage of semi crystalline plastics is high, which makes the dent problem more serious; the shrinkage of non crystalline materials is low, which will minimize the dent; the shrinkage of filling and maintaining reinforced materials is lower, and the possibility of dent is smaller.
Σχετικά με τη JasonMould Industrial Company Limited
Ο Jasonmould είναι α Κατασκευαστής καλουπιών Κίνας από πλαστικά καλούπια- καλούπι έγχυσης, καλούπια χύτευσης, πλαστική χύτευση με εμφύσηση, περιστροφική χύτευση, ιατρικός πλαστική χύτευση με έγχυση, δύο βολές πλαστική χύτευση με έγχυση, ένθετο καλούπι, υπερκαλουπώματος, χύτευση μετάλλου με έγχυση, χύτευση με μικροέγχυση, χύτευση με έγχυση σκόνης, κεραμική χύτευση με έγχυση, χύτευση με έγχυση υγρού, γεροδεμένη χύτευση με έγχυση, οικιακή μούχλα, καλούπι χύτευσης, εργαλείο καλουπιού, προσαρμοσμένα καλούπια, κινεζικά καλούπια, εργαλεία ταχείας δημιουργίας πρωτοτύπων, πλαστικά εργαλεία κατασκευής πρωτοτύπων, Εργαλεία πρέσας διάτρησης, μήτρα και εργαλεία για εξαρτήματα κινητών/κινητών τηλεφώνων, εξαρτήματα αυτοκινήτων, ηλεκτρικές σκούπες, επαναφορτιζόμενα εργαλεία, τηλέφωνα, φωτοτυπικά μηχανήματα, Υπολογιστές, ηχεία πολυμέσων, και πολλά άλλα ηλεκτρονικά προϊόντα και οικιακές συσκευές. Και επίσης κατασκευαστής πλαστικών προϊόντων, κατασκευαστής καλουπιών Κίνα- πλαστικά μέρη, πλαστική δεξαμενή νερού, πλαστικές μπάλες, Πλαστικά δοχεία, πλαστική πόρπη, πλαστική άγκυρα, πλαστική κρεμάστρα, πλαστικό κουτάλι, τοποθέτηση πλαστικών σωλήνων, πλαστικό ποτήρι, πλαστικά επιτραπέζια σκεύη, πλαστικά ποτήρια, πλαστικά μπουκάλια, πλαστικός δίσκος, πλαστικό δοχείο καλλυντικών, πλαστική θήκη, πλαστικό δοχείο τροφίμων, πλαστικές καρέκλες, πλαστικά καπάκια, πλαστικό κλείσιμο με καπάκι, πλαστικοί σωλήνες, πλαστικοί σωλήνες νερού, πλαστικά πόμολα, πλαστική σωλήνωση, πλαστικά κουτιά χρησιμότητας, πλαστικά ράφια και ούτω καθεξής.
Επικοινωνία:
Πρόσωπο: Τζέιμς Γιουάν
Εταιρία: JasonMould Industrial Company Limited
Προσθήκη: Χωριό LongGang,Πόλη LongXi,Κομητεία BoLuo,HuiZhou City,Επαρχία Γκουανγκντονγκ, Κίνα
Τηλ: 86-752-6682869
ΗΛΕΚΤΡΟΝΙΚΗ ΔΙΕΥΘΥΝΣΗ: [email protected]
Ιστοσελίδα: https://www.jasonmolding.com/custom-injection-molding/