(1) Το καλούπι πληροί τις απαιτήσεις των συνθηκών εργασίας
1. Αντοχή στη φθορά
Όταν το τυφλό έχει μετουσιωθεί πλαστικά στην κοιλότητα του καλουπιού, ρέει και γλιστράει κατά μήκος της επιφάνειας της κοιλότητας, με αποτέλεσμα σοβαρή τριβή μεταξύ της επιφάνειας της κοιλότητας και του τυφλού, resulting in the failure of the mold due to wear. Επομένως, the wear resistance of materials is one of the most basic and important properties of molds.
Hardness is the main factor affecting wear resistance. Γενικά, the higher the hardness of mold parts, the smaller the wear, and the better the wear resistance. Επιπλέον, η αντοχή στη φθορά σχετίζεται επίσης με τον τύπο, ποσότητα, σχήμα, size and distribution of carbides in the material.
2. Strength and toughness
The working conditions of molds are mostly very bad, and some often bear large impact load, resulting in brittle fracture. In order to prevent sudden brittle fracture of die parts during operation, the die should have high strength and toughness. The toughness of the die mainly depends on the carbon content, grain size and microstructure of the material.
3. Fatigue fracture performance
In the process of die working, fatigue fracture is often caused by the long-term action of cyclic stress. Its forms include small energy multiple impact fatigue fracture, tensile fatigue fracture, contact fatigue fracture and bending fatigue fracture. The fatigue fracture performance of the die mainly depends on its strength, σκληρότητα, hardness and the content of inclusions in the material.
4. High temperature performance
When the working temperature of the mold is high, the hardness and strength will decrease, resulting in early wear or plastic deformation and failure of the mold. Because the mold material should have high tempering stability, so as to ensure that the die has high hardness and strength at working temperature.
5. Cold and hot fatigue resistance
Some molds are in the state of repeated heating and cooling in the working process, so that the surface of the cavity is under the action of tensile and pressure strain stress, resulting in surface cracking and peeling, increasing friction, hindering plastic deformation and reducing dimensional accuracy, resulting in mold failure. Cold and hot fatigue is one of the main forms of hot working die failure. This kind of die should have high cold and hot fatigue resistance.
6. Αντοχή στη διάβρωση
When some molds such as plastic molds are working, due to the presence of chlorine, fluorine and other elements in the plastic, they decompose and precipitate HCI, HF and other strong corrosive gases after heating, which erode the surface of the mold cavity, increase its surface roughness and aggravate wear failure.
（2） The mold meets the process performance requirements
The manufacture of molds generally goes through several processes such as forging, cutting and heat treatment. In order to ensure the manufacturing quality of the mold and reduce the production cost, the material should have good malleability, μηχανική ικανότητα, hardenability, hardenability and grindability; It should also have small oxidation, decarburization sensitivity and quenching deformation cracking tendency.
1. Malleability
It has low hot forging deformation resistance, good plasticity, wide forging temperature range, low tendency of forging crack, cold crack and precipitation of network carbide.
2. Annealing processability
The spheroidizing annealing temperature range is wide, the annealing hardness is low and the fluctuation range is small, and the spheroidizing rate is high.
3. μηχανική ικανότητα
Large cutting parameters, low tool loss and low machining surface roughness.
4. Oxidation and decarburization sensitivity
When heated at high temperature, it has good oxidation resistance, slow decarburization speed, insensitive to heating medium and small tendency to produce pitting.
5. Hardenability
Μετά το σβήσιμο, it has uniform and high surface hardness.
6. Hardenability
Μετά το σβήσιμο, a deep hardening layer can be obtained, and it can be hardened with mild quenching medium.
7. Quenching deformation and cracking tendency
Conventional quenching has small volume change, slight shape warpage and distortion, and low tendency of abnormal deformation. Conventional quenching has low cracking sensitivity and is not sensitive to quenching temperature and workpiece shape.
8. Grindability
The grinding wheel has small relative loss, no burn limit, large grinding amount, insensitive to grinding wheel quality and cooling conditions, and is not prone to abrasion and grinding cracks.
Σχετικά με την Huizhou Dj Molding Co., Ltd
Ο Dj Mold είναι ένας Κατασκευαστής καλουπιών Κίνας από πλαστικά καλούπια- καλούπι έγχυσης, καλούπια χύτευσης, πλαστική χύτευση με εμφύσηση, περιστροφική χύτευση, ιατρικός πλαστική χύτευση με έγχυση, δύο βολές πλαστική χύτευση με έγχυση, ένθετο καλούπι, υπερκαλουπώματος, χύτευση μετάλλου με έγχυση, χύτευση με μικροέγχυση, χύτευση με έγχυση σκόνης, κεραμική χύτευση με έγχυση, χύτευση με έγχυση υγρού, γεροδεμένη χύτευση με έγχυση, οικιακή μούχλα, καλούπι χύτευσης, εργαλείο καλουπιού, προσαρμοσμένα καλούπια, κινεζικά καλούπια, εργαλεία ταχείας δημιουργίας πρωτοτύπων, πλαστικά εργαλεία κατασκευής πρωτοτύπων, Εργαλεία πρέσας διάτρησης, μήτρα και εργαλεία για εξαρτήματα κινητών/κινητών τηλεφώνων, εξαρτήματα αυτοκινήτων, ηλεκτρικές σκούπες, επαναφορτιζόμενα εργαλεία, τηλέφωνα, φωτοτυπικά μηχανήματα, Υπολογιστές, ηχεία πολυμέσων, και πολλά άλλα ηλεκτρονικά προϊόντα και οικιακές συσκευές. Και επίσης κατασκευαστής πλαστικών προϊόντων, κατασκευαστής καλουπιών Κίνα- πλαστικά μέρη, πλαστική δεξαμενή νερού, πλαστικές μπάλες, Πλαστικά δοχεία, πλαστική πόρπη, πλαστική άγκυρα, πλαστική κρεμάστρα, πλαστικό κουτάλι, τοποθέτηση πλαστικών σωλήνων, πλαστικό ποτήρι, πλαστικά επιτραπέζια σκεύη, πλαστικά ποτήρια, πλαστικά μπουκάλια, πλαστικός δίσκος, πλαστικό δοχείο καλλυντικών, πλαστική θήκη, πλαστικό δοχείο τροφίμων, πλαστικές καρέκλες, πλαστικά καπάκια, πλαστικό κλείσιμο με καπάκι, πλαστικοί σωλήνες, πλαστικοί σωλήνες νερού, πλαστικά πόμολα, πλαστική σωλήνωση, πλαστικά κουτιά χρησιμότητας, πλαστικά ράφια και ούτω καθεξής.
Επικοινωνία:
Πρόσωπο: Τζέιμς Γιουάν
Εταιρία: Huizhou Dj Molding Company Limited
Προσθήκη: Χωριό LongGang,Πόλη LongXi,Κομητεία BoLuo,HuiZhou City,Επαρχία Γκουανγκντονγκ, Κίνα
Τηλ: 86-752-6682869
ΗΛΕΚΤΡΟΝΙΚΗ ΔΙΕΥΘΥΝΣΗ: [email protected]
Ιστοσελίδα: https://www.jasonmolding.com/custom-injection-molding/