Што такое знак ракавіны?
Ўвагнутасць і след ракавіны выкліканы мясцовай ўсаджваннем, выкліканым герметызацыяй засаўкі або адсутнасцю ін'екцыі матэрыялу.
Паглыбленне або мікрапаглыбленне на паверхні ліцця пад ціскам - старая праблема ў працэсе ліцця пад ціскам. Dents are generally caused by the increase of the shrinkage rate of plastic products caused by the increase of the wall thickness. They may appear near the external sharp corner or the sudden change of the wall thickness, such as the bulge, the back of the stiffener or the support, and sometimes in some uncommon parts. The root cause of the dent is the thermal expansion and cold shrinkage of the material, because the coefficient of thermal expansion of thermoplastic is quite high. The degree of expansion and shrinkage depends on many factors, among which the plastic properties, the maximum and minimum temperature range and the cavity packing pressure are the most important factors, and the size and shape of the injection parts, the cooling rate and uniformity are also the influencing factors. Dents and shrinkage marks on plastic products are common molding defects. Каб пазбегнуць непатрэбнай траты часу і клопатаў пры масавай вытворчасці:
Аналіз і ўхіленне дэфектаў знакаў ракавіны
1) Improper control of molding conditions
If the injection pressure is too low, the injection and holding time is too short, the injection rate is too slow, the material temperature and mold temperature are too high, the cooling of the plastic part is insufficient, the temperature during demoulding is too high, the temperature at the insert is too low or the material supply is insufficient, the surface of the plastic part will appear concave or orange peel like micro unevenness. Таму, it is necessary to increase the injection pressure and injection speed, increase the compression density of the melt, extend the injection and holding time, compensate the melt shrinkage and increase the injection recoil. But the packing pressure should not be too high, otherwise it will cause convex mark.
1. If the depression and shrinkage mark occur near the gate, it can be solved by extending the holding time. The cooling time of the plastic part in the mold should be extended appropriately when the plastic part is concave at the wall thickness.
2. If the local shrinkage of the melt around the insert causes depression and shrinkage mark, which is mainly caused by the low temperature of the insert, we should try to increase the temperature of the insert.
3. If the nozzle hole of the injection molding machine is too small or the nozzle is partially blocked, the local loss of injection pressure will also cause depression and shrinkage mark. У сувязі з гэтым, the nozzle should be replaced or cleaned.
4. If the surface of plastic parts is depressed due to insufficient feeding, the feeding amount should be increased.
У дадатак, the cooling of plastic parts in the mold must be sufficient. З аднаго боку, the melt temperature can be appropriately reduced by adjusting the barrel temperature; з другога боку, the setting of the mold cooling system can be changed to reduce the temperature of the cooling water, or the cooling of the concave parts can be properly strengthened on the premise of maintaining the uniform cooling of the mold surface and all parts as far as possible. У адваротным выпадку, when the plastic part is demoulded under the condition of insufficient cooling, it is not only easy to produce shrinkage depression, but also local depression of the plastic part in the ejector due to hard demoulding.
2) Дэфекты цвілі
If the cross-section of runner and gate is too small, the mold filling resistance is too large, the gate setting is asymmetric, the mold filling speed is not balanced, the position of feed gate is not reasonable, and the mold exhaust affects the feeding, feeding and cooling, or the mold wear causes the pressure relief, it will lead to the surface depression and shrinkage mark of plastic parts. Таму, the gate and gate cross-section should be appropriately expanded according to the specific situation The gate position should be set at the symmetrical position as far as possible, and the feeding gate should be set at the thick wall of the plastic part.
If the depression and shrinkage mark occur far away from the gate, it is generally due to the poor flow of molten material in a certain part of the mold structure, which hinders the pressure transmission. Таму, the structure size of the gating system should be appropriately expanded, especially for the “bottleneck” which hinders the melt flow, the runner section must be increased, and it is better to extend the runner to the concave part.
For thick wall plastic parts, wing gate should be preferred. Такім чынам, for the plastic parts which are not suitable to set the gate directly on the plastic parts and are easy to produce residual deformation at the gate after molding, a wing body can be attached to the plastic parts, and then the gate can be set on the winglet. The gate on the winglet can use the reverse gate and the point gate, so as to transfer the concave defects of the plastic parts to the winglet, and then cut off the winglet after molding.
У дадатак, it is necessary to frequently check whether there is wear relief or poor exhaust of the mold, and timely replace the consumable parts in the mold or improve the exhaust condition of the mold.
3) Сыравіна не адпавядае патрабаванням фармоўкі
1. If the shrinkage rate of molding raw materials is too high or the flow performance is too poor, and the lubricant in the raw materials is insufficient or the raw materials are wet, the surface of the plastic parts will produce depressions and shrinkage marks. Таму, for plastic parts with high surface requirements, low shrinkage resin grade should be selected as far as possible.
2. If the underfill depression is caused by the poor flow of the molten material, an appropriate amount of lubricant can be added to the raw material to improve the fluidity of the molten material or increase the structural size of the gating system.
3. If the surface of plastic parts is depressed due to the moisture of raw materials, the raw materials should be pre dried.
4) Unreasonable shape and structure design of plastic parts
If the wall thickness of plastic parts varies greatly, the thick wall parts are prone to depression and shrinkage marks due to insufficient pressure. Таму, when designing the shape and structure of plastic parts, the wall thickness should be as consistent as possible. For special cases, if the wall thickness of plastic parts is different, it can be solved by adjusting the structural parameters of the gating system.
Аб JasonMould Industrial Company Limited
і выкарыстоўваць азот для ачысткі ўнутранай часткі гідраўлічнага блока цыліндраў фармовачнай машыны, каб вырашыць праблему наліпанне на паверхні прадукту і выкарыстоўваць азот для ачысткі ўнутранай часткі гідраўлічнага блока цыліндраў фармовачнай машыны, каб вырашыць праблему наліпанне на паверхні прадукту і выкарыстоўваць азот для ачысткі ўнутранай часткі гідраўлічнага блока цыліндраў фармовачнай машыны, каб вырашыць праблему наліпанне на паверхні прадукту- ліццёвая форма, формы для ліцця пад ціскам, фармаванне пластыкам, ратацыйнае ліццё, медыцынскія ліццё пад ціскам з пластыка, два стрэлы ліццё пад ціскам з пластыка, ўстаўка ліццё, ліццё пад ціскам, ліццё пад ціскам металу, мікра ліццё пад ціскам, ліццё парашка, ліццё пад кераміку, ліццё пад ціскам вадкасці, ліццё з лайка, бытавая цвіль, форма для ліцця, інструмент для прэс -формы, нестандартныя формы, фарфоры для фарфору, хуткае стварэнне прататыпаў, інструменты для прататыпавання пластыка, інструмент для прабівання прэса, матрыца і інструменты для дэталяў мабільнага тэлефона/ мабільнага тэлефона, аўтамабільныя запчасткі, пыласосы, акумулятарныя інструменты, тэлефоны, ксераксы, кампутары, мультымедыйныя калонкі, і многія іншыя электронныя вырабы і бытавая тэхніка. А таксама вытворца пластыкавых вырабаў, і выкарыстоўваць азот для ачысткі ўнутранай часткі гідраўлічнага блока цыліндраў фармовачнай машыны, каб вырашыць праблему наліпанне на паверхні прадуктуі выкарыстоўваць азот для ачысткі ўнутранай часткі гідраўлічнага блока цыліндраў фармовачнай машыны, каб вырашыць праблему наліпанне на паверхні прадукту, пластыкавы бак для вады, пластыкавыя шары, пластыкавыя кантэйнеры, пластыкавая спражка, якар з пластыка, пластыкавая вешалка, пластыкавая лыжка, пластыкавы фітынг труб, пластыкавы кавалак, пластыкавы посуд, пластыкавыя шкляначкі, пластыкавыя бутэлькі, пластыкавы латок, пластыкавы касметычны кантэйнер, пластыкавы корпус, пластыкавы кантэйнер для ежы, пластыкавыя крэслы, пластыкавыя каўпачкі, пластыкавы каўпачок, пластыкавыя трубкі, пластыкавыя водаправодныя трубы, пластыкавыя ручкі, пластыкавыя трубкі, пластыкавыя скрыні для гаспадарчых машын, пластыкавыя стойкі і гэтак далей.
Кантакт:
Асоба: Джэймс Юань
Кампанія: JasonMould Industrial Company Limited
Дадаць: Вёска LongGang,Горад LongXi,Акруга БоЛуо,Горад Хуэйчжоу,Правінцыя Гуандун, Кітай
Тэл: 86-752-6682869
Электронная пошта: [email protected]
Сайт: https://www.jasonmolding.com/custom-injection-molding/