ABS, шырока вядомы як акрыланітрыл-бутадыен-стырол, вырабляецца шляхам супалімерызацыі акрыланітрылу бутадыенстыролу. З-за розных прапорцый трох мономеров, АБС з рознымі ўласцівасцямі і тэмпературай плаўлення можа быць пашыраны ў АБС з розным выкарыстаннем і ўласцівасцямі, напрыклад, ступень ўздзеяння, клас цеплаўстойлівасці, гатунак вогнеахоўнага, празрысты гатунак, узмоцнены гатунак, гатунак гальванікі, пазіцыянаванне і, калі ён змешаны з іншымі пластмасамі або дадаткамі.
Плыўнасць ABS знаходзіцца паміж PS і PC. the fluidity of ABS is related to injection temperature and pressure. The influence of injection pressure is slightly greater. Таму, higher injection pressure is often used to reduce melt viscosity and improve filling performance.
1. Treatment of plastics
The water absorption rate of ABS is about 0.2% – 0.8%. For general grade ABS, bake in oven at 80-85 ℃ для 2-4 hours or in drying hopper at 80 ℃ для 1-2 hours before processing. For heat-resistant ABS with PC component, the drying temperature should be adjusted to 100 ℃, and the specific drying time can be determined by extrusion. Доля перапрацаваных матэрыялаў не павінна перавышаць 30%, and the recycled materials should not be used for electroplating ABS.
2. Selection of injection molding machine
The standard injection molding machine of Ramada can be selected (the length diameter ratio of screw is 20:1, the compression ratio is greater than 2, and the injection pressure is greater than 1500bar). If the color masterbatch is used or the appearance of the product is high, the screw with a smaller diameter can be selected. The clamping force is determined according to 4700-6200t / m2, which depends on the plastic grade and product requirements.
3. Канструкцыя формы і варот
Mold temperature can be set at 60-65 ℃. The channel diameter is 6-8mm. The gate width is about 3 мм, the thickness is the same as the product, and the gate length is less than 1 мм. The exhaust hole is 4-6mm wide and 0.025-0.05mm thick.
4. Тэмпература расплаву
It can be accurately determined by air injection. According to different grades, the melt temperature is also different. It is suggested to set as follows:
Impact grade: 220 ℃ – 260 ℃, 250 ℃ is better
Electroplating grade: 250 ℃ – 275 ℃, 270 ℃ is better
Heat resistant grade: 240 ℃ – 280 ℃, 265 ℃ – 270 ℃
Flame retardant grade: 200 ℃ – 240 ℃, 220 ℃ – 230 ℃ is better
Transparent grade: 230 ℃ – 260 ℃, 245 ℃ is better
Glass fiber reinforced grade: 230 ℃ – 270 ℃
For products with high surface requirements, higher melt temperature and mold temperature are used.
5. Injection rate
The fire grade should use slow speed, and the heat grade should use fast speed. If the surface requirement of the product is high, the shooting speed of high-speed and multi-stage injection should be controlled.
6. Back pressure
Увогуле, the lower the back pressure is, the better. The commonly used back pressure is 5bar. The dyeing material needs higher back pressure to make the color mixing uniform.
7. Residence time
At 265 ℃, the residence time of ABS in the melt can not exceed 5-6 minutes at most. The flame retardant time is shorter. If the machine needs to be stopped, the set temperature should be lowered to 100 ℃ first, and then the general-purpose ABS can be used to clean the glue cartridge. The cleaned mixture should be put into cold water to prevent further decomposition. If you need to change from other plastics to ABS material, you need to use PS, PMMA or PE to clean the glue cartridge. Some ABS products have no problem when they are just demoulded, and they will change color after a period of time, which may be caused by overheating or too long residence time of the plastic in the melt cartridge.
8. Post treatment of products
General ABS products do not need post-treatment, only electroplating grade products need to be baked (70-80 ℃, 2-4 гадзіны) to passivate the surface traces, and the products that need to be electroplated can not use mold release agent, and the products should be packed immediately after they are taken out.
9. Matters needing special attention during molding
There are several grades of ABS (especially flame retardant grade). After plasticization, the adhesive force of the melt on the screw surface is very large, and it will decompose after a long time. When the above situation occurs, it is necessary to pull the homogenizing section and compression screw out for wiping test, and regularly clean the screw with PS, і г.д..
Аб JasonMould Industrial Company Limited
і выкарыстоўваць азот для ачысткі ўнутранай часткі гідраўлічнага блока цыліндраў фармовачнай машыны, каб вырашыць праблему наліпанне на паверхні прадукту і выкарыстоўваць азот для ачысткі ўнутранай часткі гідраўлічнага блока цыліндраў фармовачнай машыны, каб вырашыць праблему наліпанне на паверхні прадукту і выкарыстоўваць азот для ачысткі ўнутранай часткі гідраўлічнага блока цыліндраў фармовачнай машыны, каб вырашыць праблему наліпанне на паверхні прадукту- ліццёвая форма, формы для ліцця пад ціскам, фармаванне пластыкам, ратацыйнае ліццё, медыцынскія ліццё пад ціскам з пластыка, два стрэлы ліццё пад ціскам з пластыка, ўстаўка ліццё, ліццё пад ціскам, ліццё пад ціскам металу, мікра ліццё пад ціскам, ліццё парашка, ліццё пад кераміку, ліццё пад ціскам вадкасці, ліццё з лайка, бытавая цвіль, форма для ліцця, інструмент для прэс -формы, нестандартныя формы, фарфоры для фарфору, хуткае стварэнне прататыпаў, інструменты для прататыпавання пластыка, інструмент для прабівання прэса, матрыца і інструменты для дэталяў мабільнага тэлефона/ мабільнага тэлефона, аўтамабільныя запчасткі, пыласосы, акумулятарныя інструменты, тэлефоны, ксераксы, кампутары, мультымедыйныя калонкі, і многія іншыя электронныя вырабы і бытавая тэхніка. А таксама вытворца пластыкавых вырабаў, і выкарыстоўваць азот для ачысткі ўнутранай часткі гідраўлічнага блока цыліндраў фармовачнай машыны, каб вырашыць праблему наліпанне на паверхні прадуктуі выкарыстоўваць азот для ачысткі ўнутранай часткі гідраўлічнага блока цыліндраў фармовачнай машыны, каб вырашыць праблему наліпанне на паверхні прадукту, пластыкавы бак для вады, пластыкавыя шары, пластыкавыя кантэйнеры, пластыкавая спражка, якар з пластыка, пластыкавая вешалка, пластыкавая лыжка, пластыкавы фітынг труб, пластыкавы кавалак, пластыкавы посуд, пластыкавыя шкляначкі, пластыкавыя бутэлькі, пластыкавы латок, пластыкавы касметычны кантэйнер, пластыкавы корпус, пластыкавы кантэйнер для ежы, пластыкавыя крэслы, пластыкавыя каўпачкі, пластыкавы каўпачок, пластыкавыя трубкі, пластыкавыя водаправодныя трубы, пластыкавыя ручкі, пластыкавыя трубкі, пластыкавыя скрыні для гаспадарчых машын, пластыкавыя стойкі і гэтак далей.
Кантакт:
Асоба: Джэймс Юань
Кампанія: JasonMould Industrial Company Limited
Дадаць: Вёска LongGang,Горад LongXi,Акруга БоЛуо,Горад Хуэйчжоу,Правінцыя Гуандун, Кітай
Тэл: 86-752-6682869
Электронная пошта: [email protected]
Сайт: https://www.jasonmolding.com/custom-injection-molding/