La dureza del tratamiento térmico del molde es un índice de propiedad mecánica muy importante., Y la dureza incondicional es un defecto muy grave.. Una dureza insuficiente o desigual después del tratamiento térmico reducirá la resistencia al desgaste y la resistencia a la fatiga del molde., conducir a la falla temprana del molde, y reducir seriamente la vida útil del molde.
- Causas
1) La sección transversal del molde es grande y la templabilidad del acero es pobre.. Por ejemplo, the steel with low hardenability is selected for the large-scale mould.
2) Carbide segregation is serious or coarse in the original structure of die steel. Graphite carbon and carbide segregation and aggregation exist in the steel.
3) The forging process of the mould is incorrect, and no good spheroidizing annealing is carried out after forging, resulting in poor spheroidizing structure of the mould steel.
4) The decarburization layer on the surface of the mould is not removed by annealing or quenching heating.
5) Excessive quenching temperature and excessive retained austenite after quenching, or too low quenching temperature and insufficient heating and holding time make the phase transformation of mould steel incomplete.
6) After quenching and heating, the cooling speed of the mould is too slow, the grading and isothermal temperature are too high or the time is too long, and the selection of quenching cooling medium is inappropriate.
7) too little water in alkali bath or too much impurity in quenching cooling medium or aging of quenching cooling medium.
8) Temperature is too high and cooling is insufficient when the quenching cooling medium is released after quenching and cooling of the mould.
9) insufficient tempering and high tempering temperature.
- Countermeasures
1) Correct selection of mould steel, large-scale mould should choose high alloy mould steel with high hardenability.
2) Strengthen the inspection of raw materials to ensure that raw materials meet the standards. Reasonable forging and spheroidizing annealing are carried out on the steel with bad raw materials to ensure good structure. Carbon tool steels are not easily annealed many times to prevent graphitization.
3) Strict implementation of forging and spheroidizing annealing processes to ensure a good preparation of heat treatment structure.
4) Before heat treatment, rust spots and oxide scales on the surface of the mould should be thoroughly removed, and attention should be paid to the protection during heating. Vacuum heating quenching or protective atmosphere heating quenching should be adopted as far as possible, and good deoxidization treatment should be carried out when salt bath heating.
5) Correctly formulate the process parameters of quenching and heating of the die to ensure that the phase transformation is sufficient and the cooling speed is faster than the critical cooling speed to obtain qualified metallographic structure.
6) Correct selection of quenching medium and cooling mode, strict control of classification and isothermal temperature and time.
7) The water content of alkali bath should be strictly controlled. The quenching cooling medium used for a long time should be filtered and replaced regularly, and kept clean. The quenching cooling characteristic curve should be tested regularly.
8) For large-sized moulds, the time of immersion in quenching cooling medium should be prolonged to prevent the temperature of quenching cooling medium from being too high.
9) Después de apagar, the mould should be tempered promptly and sufficiently, and the tempering temperature should be prevented from being too high.
10) The mould with high hardness requirement can be treated by cryogenic treatment (Con la tecnología de proceso de control numérico del centro de mecanizado CNC. – 110 ~196 C).
11) Surface strengthening.
JasonMould Industrial Company Limited, establecido en 2010, se debe prestar especial atención a la limpieza del molde se debe prestar especial atención a la limpieza del molde. JasonMould se especializa en la producción de moldes de plástico para electrodomésticos., equipos medicos, equipos electronicos, equipos de seguridad y sistema de monitorización.
La empresa ha terminado 15000 fábrica de metros cuadrados. Con divisiones de herramientas de inyección de plástico que poseen diferentes maquinarias y experiencia., JasonMould ofrece herramientas desde piezas pequeñas y precisas para teléfonos móviles hasta piezas tan grandes como piezas de automóviles.. Nuestras herramientas se exportan principalmente a EE. UU., Europa, Japón y Reino Unido. La estrategia de diversificación y el servicio completo de JasonMould se han ganado elogios de clientes de todo el mundo..
Nuestra misión es proporcionar a nuestros clientes productos y servicios de moldeo de alta calidad.. Nuestro objetivo es superar las expectativas de precios de nuestros clientes., calidad y entrega a tiempo. Para lograr nuestra misión, JasonMould:
- Se compromete a mejorar continuamente las habilidades y la eficiencia de los empleados.,
- Proporciona a nuestros empleados un entorno de trabajo limpio y seguro.,
- Actualiza la tecnología de la máquina y el equipo de soporte a través de un estricto programa de mantenimiento., y
- Mantiene las herramientas de los clientes en su pico más alto de rendimiento.
En comparación con cualquier otra técnica en el mercado Costo de moldeo por inyección de China,por favor visita https://www.jasonmolding.com/
Contacto de consulta:
Persona de contacto: James Yuan
Nombre de empresa: JasonMould Industrial Company Limited
Habla a: Pueblo LongGang,Ciudad de LongXi,Condado de BoLuo,Ciudad de HuiZhou,La provincia de Guangdong, porcelana
Teléfono: 86-752-6682869
Correo electrónico: [email protected]
Sitio web: https://www.jasonmolding.com