Duritatea tratamentului termic al matriței este un indice de proprietăți mecanice foarte important, iar duritatea necalificată este un defect foarte grav. Duritatea insuficientă sau duritatea neuniformă după tratamentul termic va reduce rezistența la uzură și rezistența la oboseală a matriței, duce la defectarea timpurie a matriței, și reduce serios durata de viață a matriței.
- Cauze
1) Secțiunea transversală a matriței este mare și călibilitatea oțelului este slabă. De exemplu, the steel with low hardenability is selected for the large-scale mould.
2) Carbide segregation is serious or coarse in the original structure of die steel. Graphite carbon and carbide segregation and aggregation exist in the steel.
3) The forging process of the mould is incorrect, and no good spheroidizing annealing is carried out after forging, resulting in poor spheroidizing structure of the mould steel.
4) The decarburization layer on the surface of the mould is not removed by annealing or quenching heating.
5) Excessive quenching temperature and excessive retained austenite after quenching, or too low quenching temperature and insufficient heating and holding time make the phase transformation of mould steel incomplete.
6) After quenching and heating, the cooling speed of the mould is too slow, the grading and isothermal temperature are too high or the time is too long, and the selection of quenching cooling medium is inappropriate.
7) too little water in alkali bath or too much impurity in quenching cooling medium or aging of quenching cooling medium.
8) Temperature is too high and cooling is insufficient when the quenching cooling medium is released after quenching and cooling of the mould.
9) insufficient tempering and high tempering temperature.
- Countermeasures
1) Correct selection of mould steel, large-scale mould should choose high alloy mould steel with high hardenability.
2) Strengthen the inspection of raw materials to ensure that raw materials meet the standards. Reasonable forging and spheroidizing annealing are carried out on the steel with bad raw materials to ensure good structure. Carbon tool steels are not easily annealed many times to prevent graphitization.
3) Strict implementation of forging and spheroidizing annealing processes to ensure a good preparation of heat treatment structure.
4) Before heat treatment, rust spots and oxide scales on the surface of the mould should be thoroughly removed, and attention should be paid to the protection during heating. Vacuum heating quenching or protective atmosphere heating quenching should be adopted as far as possible, and good deoxidization treatment should be carried out when salt bath heating.
5) Correctly formulate the process parameters of quenching and heating of the die to ensure that the phase transformation is sufficient and the cooling speed is faster than the critical cooling speed to obtain qualified metallographic structure.
6) Correct selection of quenching medium and cooling mode, strict control of classification and isothermal temperature and time.
7) The water content of alkali bath should be strictly controlled. The quenching cooling medium used for a long time should be filtered and replaced regularly, and kept clean. The quenching cooling characteristic curve should be tested regularly.
8) For large-sized moulds, the time of immersion in quenching cooling medium should be prolonged to prevent the temperature of quenching cooling medium from being too high.
9) După stingere, the mould should be tempered promptly and sufficiently, and the tempering temperature should be prevented from being too high.
10) The mould with high hardness requirement can be treated by cryogenic treatment (de exemplu. – 110 ~196 C).
11) Surface strengthening.
JasonMould Industrial Company Limited, stabilit in 2010, este un lider Fabrica de mucegai din China. JasonMould este specializat în producția de matrițe din plastic pentru aparatele de uz casnic, echipamente medicale, echipamente electronice, echipamente de siguranță, precum și sistem de monitorizare.
Compania a terminat 15000 fabrica de metri patrati. Cu divizii de scule de injecție cu plastic care posedă utilaje și expertiză diferite, JasonMould oferă instrumente de la piese mici și precise pentru telefoane mobile până la piese de dimensiuni mari precum piese auto. Instrumentele noastre sunt exportate în principal în S.U.A., Europa, Japonia și Marea Britanie. Strategia de diversificare a lui JasonMould și serviciile complete au câștigat complimente din partea clienților din întreaga lume.
Misiunea noastră este de a oferi clienților noștri produse și servicii de turnare de înaltă calitate. Ne propunem să depășim așteptările clienților noștri cu privire la prețuri, calitate și livrare la timp. Pentru a ne îndeplini misiunea, JasonMould:
- Se angajează să îmbunătățească continuu abilitățile și eficiența angajaților,
- Oferă angajaților noștri un mediu de lucru curat și sigur,
- Îmbunătățește tehnologia mașinilor și echipamentele de asistență printr-un program strict de întreținere, și
- Menține uneltele clienților la cel mai înalt vârf de performanță
Pentru mai multe despre Costul turnării prin injecție în China,Tehnologia Hot Runner nu face excepție https://www.jasonmolding.com/
Întrebare Contact:
Persoană de contact: James Yuan
Numele companiei: JasonMould Industrial Company Limited
Abordare: Satul LongGang,Orașul LongXi,Județul BoLuo,Orașul HuiZhou,Provincia Guangdong, China
Telefon: 86-752-6682869
E-mail: [email protected]
Site-ul web: https://www.jasonmolding.com