ความแข็งของการอบชุบด้วยความร้อนของแม่พิมพ์เป็นดัชนีคุณสมบัติทางกลที่สำคัญมาก, และความแข็งอย่างไม่มีเงื่อนไขเป็นข้อบกพร่องที่ร้ายแรงมาก. ความแข็งไม่เพียงพอหรือความแข็งไม่สม่ำเสมอหลังจากการอบชุบด้วยความร้อนจะลดความต้านทานการสึกหรอและความล้าของแม่พิมพ์, lead to early failure of the mould, and seriously reduce the service life of the mould.
- สาเหตุ
1) The cross-section of the mould is large and the hardenability of the steel is poor. ตัวอย่างเช่น, the steel with low hardenability is selected for the large-scale mould.
2) Carbide segregation is serious or coarse in the original structure of die steel. Graphite carbon and carbide segregation and aggregation exist in the steel.
3) The forging process of the mould is incorrect, and no good spheroidizing annealing is carried out after forging, resulting in poor spheroidizing structure of the mould steel.
4) The decarburization layer on the surface of the mould is not removed by annealing or quenching heating.
5) Excessive quenching temperature and excessive retained austenite after quenching, or too low quenching temperature and insufficient heating and holding time make the phase transformation of mould steel incomplete.
6) After quenching and heating, the cooling speed of the mould is too slow, the grading and isothermal temperature are too high or the time is too long, and the selection of quenching cooling medium is inappropriate.
7) too little water in alkali bath or too much impurity in quenching cooling medium or aging of quenching cooling medium.
8) Temperature is too high and cooling is insufficient when the quenching cooling medium is released after quenching and cooling of the mould.
9) insufficient tempering and high tempering temperature.
- Countermeasures
1) Correct selection of mould steel, large-scale mould should choose high alloy mould steel with high hardenability.
2) Strengthen the inspection of raw materials to ensure that raw materials meet the standards. Reasonable forging and spheroidizing annealing are carried out on the steel with bad raw materials to ensure good structure. Carbon tool steels are not easily annealed many times to prevent graphitization.
3) Strict implementation of forging and spheroidizing annealing processes to ensure a good preparation of heat treatment structure.
4) Before heat treatment, rust spots and oxide scales on the surface of the mould should be thoroughly removed, and attention should be paid to the protection during heating. Vacuum heating quenching or protective atmosphere heating quenching should be adopted as far as possible, and good deoxidization treatment should be carried out when salt bath heating.
5) Correctly formulate the process parameters of quenching and heating of the die to ensure that the phase transformation is sufficient and the cooling speed is faster than the critical cooling speed to obtain qualified metallographic structure.
6) Correct selection of quenching medium and cooling mode, strict control of classification and isothermal temperature and time.
7) The water content of alkali bath should be strictly controlled. The quenching cooling medium used for a long time should be filtered and replaced regularly, and kept clean. The quenching cooling characteristic curve should be tested regularly.
8) For large-sized moulds, the time of immersion in quenching cooling medium should be prolonged to prevent the temperature of quenching cooling medium from being too high.
9) หลังจากดับ, the mould should be tempered promptly and sufficiently, and the tempering temperature should be prevented from being too high.
10) The mould with high hardness requirement can be treated by cryogenic treatment (เช่น. – 110 ~196 C).
11) Surface strengthening.
JasonMould Industrial Company Limited, ก่อตั้งขึ้นใน 2010, เป็นผู้นำ โรงงานแม่พิมพ์จีน. JasonMould เชี่ยวชาญด้านการผลิตแม่พิมพ์พลาสติกสำหรับเครื่องใช้ในครัวเรือน, อุปกรณ์ทางการแพทย์, อุปกรณ์อิเล็กทรอนิกส์, อุปกรณ์ความปลอดภัยพร้อมทั้งระบบตรวจสอบ.
บริษัทมีมากกว่า 15000 ตารางเมตร โรงงาน. ด้วยแผนกเครื่องมือฉีดพลาสติกที่มีเครื่องจักรและความชำนาญต่างกัน, JasonMould นำเสนอเครื่องมือตั้งแต่ชิ้นส่วนโทรศัพท์มือถือขนาดเล็กและแม่นยำไปจนถึงขนาดใหญ่เท่าชิ้นส่วนยานยนต์. เครื่องมือของเราส่วนใหญ่ส่งออกไปยังสหรัฐอเมริกา, ยุโรป, ญี่ปุ่นและสหราชอาณาจักร. กลยุทธ์การกระจายความเสี่ยงและบริการเต็มรูปแบบของ JasonMould ได้รับคำชมจากลูกค้าทั่วโลก.
ภารกิจของเราคือการจัดหาผลิตภัณฑ์และบริการแม่พิมพ์คุณภาพสูงแก่ลูกค้าของเรา. เรามุ่งมั่นที่จะเกินความคาดหวังของลูกค้าในด้านราคา, คุณภาพและการส่งมอบตรงเวลา. เพื่อให้บรรลุภารกิจของเรา, JasonMould:
- มุ่งมั่นพัฒนาทักษะและประสิทธิภาพของพนักงานอย่างต่อเนื่อง,
- ให้พนักงานของเรามีสภาพแวดล้อมการทำงานที่สะอาดและปลอดภัย,
- อัพเกรดเทคโนโลยีเครื่องจักรและอุปกรณ์สนับสนุนผ่านโปรแกรมการบำรุงรักษาที่เข้มงวด, และ
- รักษาเครื่องมือของลูกค้าให้มีประสิทธิภาพสูงสุด
ข้อมูลเพิ่มเติมเกี่ยวกับ ต้นทุนการฉีดขึ้นรูปของจีน,กรุณาเยี่ยมชม https://www.jasonmolding.com/
ติดต่อสอบถาม:
บุคคลที่ติดต่อ: เจมส์ หยวน
ชื่อ บริษัท: JasonMould Industrial Company Limited
ที่อยู่: หมู่บ้านหลงกัง,เมืองหลงซี,BoLuo County,เมืองฮุ่ยโจว,มณฑลกวางตุ้ง, ประเทศจีน
โทรศัพท์: 86-752-6682869
อีเมล: [email protected]
เว็บไซต์: https://www.jasonmolding.com