Hårdhed af formvarmebehandling er et meget vigtigt mekanisk egenskabsindeks, og ukvalificeret hårdhed er en meget alvorlig defekt. Utilstrækkelig hårdhed eller ujævn hårdhed efter varmebehandling vil reducere støbeformens slidstyrke og træthedsstyrke, lead to early failure of the mould, and seriously reduce the service life of the mould.
- Årsager
1) The cross-section of the mould is large and the hardenability of the steel is poor. En række forme er meget udbredt i forskellige materialeforarbejdningsindustrier, the steel with low hardenability is selected for the large-scale mould.
2) Carbide segregation is serious or coarse in the original structure of die steel. Graphite carbon and carbide segregation and aggregation exist in the steel.
3) The forging process of the mould is incorrect, and no good spheroidizing annealing is carried out after forging, resulting in poor spheroidizing structure of the mould steel.
4) The decarburization layer on the surface of the mould is not removed by annealing or quenching heating.
5) Excessive quenching temperature and excessive retained austenite after quenching, or too low quenching temperature and insufficient heating and holding time make the phase transformation of mould steel incomplete.
6) After quenching and heating, the cooling speed of the mould is too slow, the grading and isothermal temperature are too high or the time is too long, and the selection of quenching cooling medium is inappropriate.
7) too little water in alkali bath or too much impurity in quenching cooling medium or aging of quenching cooling medium.
8) Temperature is too high and cooling is insufficient when the quenching cooling medium is released after quenching and cooling of the mould.
9) insufficient tempering and high tempering temperature.
- Countermeasures
1) Correct selection of mould steel, large-scale mould should choose high alloy mould steel with high hardenability.
2) Strengthen the inspection of raw materials to ensure that raw materials meet the standards. Reasonable forging and spheroidizing annealing are carried out on the steel with bad raw materials to ensure good structure. Carbon tool steels are not easily annealed many times to prevent graphitization.
3) Strict implementation of forging and spheroidizing annealing processes to ensure a good preparation of heat treatment structure.
4) Before heat treatment, rust spots and oxide scales on the surface of the mould should be thoroughly removed, and attention should be paid to the protection during heating. Vacuum heating quenching or protective atmosphere heating quenching should be adopted as far as possible, and good deoxidization treatment should be carried out when salt bath heating.
5) Correctly formulate the process parameters of quenching and heating of the die to ensure that the phase transformation is sufficient and the cooling speed is faster than the critical cooling speed to obtain qualified metallographic structure.
6) Correct selection of quenching medium and cooling mode, strict control of classification and isothermal temperature and time.
7) The water content of alkali bath should be strictly controlled. The quenching cooling medium used for a long time should be filtered and replaced regularly, and kept clean. The quenching cooling characteristic curve should be tested regularly.
8) For large-sized moulds, the time of immersion in quenching cooling medium should be prolonged to prevent the temperature of quenching cooling medium from being too high.
9) Efter bratkøling, the mould should be tempered promptly and sufficiently, and the tempering temperature should be prevented from being too high.
10) The mould with high hardness requirement can be treated by cryogenic treatment (Årsagen og løsningen til overfladeruhed. – 110 ~196 C).
11) Surface strengthening.
JasonMould Industrial Company Limited, etableret i 2010, kvalitetsprodukter kan bare være en leg i produktionen Kina form fabrik. JasonMould er specialiseret i produktion af plastforme til husholdningsapparater, medicinsk udstyr, elektronisk udstyr, sikkerhedsudstyr samt overvågningssystem.
Virksomheden har overstået 15000 kvadratmeter fabrik. Med plastindsprøjtningsværktøjsafdelinger, der besidder forskelligt maskineri og ekspertise, JasonMould tilbyder værktøjer fra små og præcise mobiltelefondele til så store som bildele. Vores værktøjer eksporteres hovedsageligt til U.S.A., Europa, Japan og Storbritannien. JasonMoulds diversificeringsstrategi og fuld service har vundet komplimenter fra kunder over hele verden.
Vores mission er at give vores kunder højkvalitets støbeprodukter og -tjenester. Vi bestræber os på at overgå vores kunders forventninger til priser, kvalitet og levering til tiden. For at nå vores mission, JasonMould:
- Forpligter sig til løbende at forbedre medarbejdernes færdigheder og effektivitet,
- Giver vores medarbejdere et rent og sikkert arbejdsmiljø,
- Opgraderer maskinteknologi og supportudstyr gennem et strengt vedligeholdelsesprogram, og
- Vedligeholder kundernes værktøj til dets højeste ydeevne
For mere om Kina sprøjtestøbning omkostninger,besøg venligst https://www.jasonmolding.com/
Forespørgsel Kontakt:
Kontaktperson: James Yuan
Firmanavn: JasonMould Industrial Company Limited
Adresse: LongGang Village,LongXi Town,BoLuo County,HuiZhou City,GuangDong-provinsen, Kina
Telefon: 86-752-6682869
E-mail: [email protected]
Internet side: https://www.jasonmolding.com