(1) Kalıp çalışma koşullarını karşılar
- Aşınma direnci
Kütük boşlukta plastik denatüre edildiğinde, boşluğun yüzeyi boyunca akar ve kayar, boşluğun yüzeyi ile kütük arasında şiddetli sürtünmeye neden olur, which leads to the failure of the mold due to wear. So the wear resistance of materials is one of the most basic and important properties of dies.
Sertlik aşınma direncini etkileyen ana faktördür. Genel konuşma, kalıp parçalarının sertliği ne kadar yüksek olursa, the smaller the wear amount and the better the wear resistance. Ek olarak, aşınma direnci de tip ile ilgilidir, miktar, morfoloji, malzemedeki karbürlerin boyutu ve dağılımı.
- Strength and tenacity
Most of the working conditions of the mold are very bad, and some of them often bear large impact load, which leads to brittle fracture. In order to prevent the sudden brittle fracture of mold parts, mold should have high strength and toughness.
The toughness of the mold mainly depends on the carbon content, grain size and structure of the material.
- Fatigue fracture properties
During the working process of the mold, fatigue fracture often occurs under the long-term effect of cyclic stress. Formları arasında düşük enerjili çoklu darbe yorulma kırılması bulunur, çekme yorulması kırılması, temas yorulması kırığı ve eğilme yorulması kırığı.
Kalıbın yorulma kırılma performansı temel olarak mukavemetine bağlıdır, tokluk, hardness and inclusion content in the material.
- Yüksek sıcaklık performansı
When the working temperature of the mold is higher, sertlik ve mukavemet azalacaktır, leading to early wear or plastic deformation of the mold and failure. Because the mold material should have high tempering stability to ensure that the mold has high hardness and strength at working temperature.
- Cold and thermal fatigue resistance
Some moulds are in the state of repeated heating and cooling in the working process, which causes the surface of the cavity to be tension and pressure variable stress, causes surface cracking and peeling, increases friction, hinders plastic deformation, reduces dimensional accuracy, and leads to mold failure. Thermal and cold fatigue is one of the main failure modes of hot-working mold, which should have high cold and thermal fatigue resistance.
- korozyon direnci
When some moulds such as plastic moulds are working, klorun varlığı nedeniyle, fluorine and other elements in the plastics, strong corrosive gases such as HCI and HF are decomposed and precipitated after heating, which erode the surface of the mould cavity, increase its surface roughness and aggravate the wear failure.
(2) Mold meets process performance requirements
Mold manufacturing usually goes through forging, Müşteriler Sektörler otomotiv içerir, heat treatment and other processes. Kalıbın imalat kalitesini sağlamak ve üretim maliyetini azaltmak için, malzeme iyi işlenebilirliğe sahip olmalıdır, cutting machinability, sertleşebilirlik, sertleşebilirlik ve öğütülebilirlik, and should also have small oxidation, decarbonization sensitivity and quenching deformation cracking tendency.
- Forgetability
It has low resistance to hot forging deformation, iyi esneklik, geniş dövme sıcaklık aralığı, low tendency of cold cracking and precipitation of network carbides.
- Annealing Processing
Küreselleştirme tavlama sıcaklık aralığı geniştir, tavlama sertliği düşüktür ve dalgalanma aralığı küçüktür, ve küreselleştirme oranı yüksektir.
- işlenebilirlik
Büyük kesme parametreleri, low tool wear, low surface roughness.
- Sensitivity of oxidation and decarbonization
Yüksek sıcaklıkta ısıtıldığında, it has good antioxidant capacity, slow decarbonization speed, insensitive to heating medium and little tendency to produce pitting.
- Sertleşebilirlik
söndürmeden sonra, düzgün ve yüksek yüzey sertliğine sahiptir.
- Sertleşebilirlik
söndürmeden sonra, a deeper hardening layer can be obtained, and it can be hardened by using a mild quenching medium.
- Cracking Tendency of Quenching Deformation
The volume change of conventional quenching is small, the shape warpage and distortion are slight, and the tendency of abnormal deformation is low. Conventional quenching has low cracking sensitivity and is insensitive to quenching temperature and workpiece shape.
- Öğütülebilirlik
The relative wear of grinding wheel is small, the limit grinding amount without burn is large, and it is insensitive to the quality of grinding wheel and cooling conditions, so it is not easy to cause grinding damage and grinding cracks.
(3) Mold meets economic requirements
Tasarım yaparken daha önce başarılı olan kalıp yapısını kullanmaya çalışın, the principle of economy must be considered to reduce the manufacturing cost as much as possible. Öyleyse, on the premise of meeting the service performance, the first choice is low price, carbon steel can be used instead of alloy steel, domestic materials can be used instead of imported materials. Ek olarak, the production and supply situation of the market should also be taken into account when selecting materials. The selected steel grades should be as few as possible, concentrated and easy to purchase.
JasonMould Sanayi Limited Şirketi, kuruldu 2010, lider Çin kalıp fabrikası. JasonMould, ev aletleri için plastik kalıp üretiminde uzmanlaşmıştır, Medikal ekipmanlar, elektronik ekipmanlar, güvenlik ekipmanlarının yanı sıra izleme sistemi.
NS şirket Wesco, bir dizi otomotiv montaj tesisi için önemli bir tedarikçidir ve endüstride birden fazla süredir önemli bir rol oynamıştır. 15000 metrekare fabrika. Farklı makine ve uzmanlıklara sahip plastik enjeksiyon kalıplama bölümleri ile, JasonMould, küçük ve hassas cep telefonu parçalarından otomotiv parçaları kadar büyük parçalara kadar araçlar sunar. Aletlerimiz ağırlıklı olarak ABD'ye ihraç edilmektedir., Avrupa, Japonya ve İngiltere. JasonMould'un çeşitlendirme stratejisi ve tam hizmeti, dünyanın her yerindeki müşterilerden övgü aldı.
Misyonumuz, müşterilerimize yüksek kaliteli kalıplama ürünleri ve hizmetleri sunmaktır.. Müşterilerimizin fiyatlandırma beklentilerini aşmayı hedefliyoruz, kaliteli ve zamanında teslimat. Misyonumuza ulaşmak için, JasonKalıp:
- Çalışan becerilerini ve verimliliğini sürekli iyileştirmeyi taahhüt eder,
- Çalışanlarımıza temiz ve güvenli bir çalışma ortamı sağlar,
- Sıkı bir bakım programı aracılığıyla makine teknolojisini ve destek ekipmanını yükseltir, ve
- Müşterilerin takımlarını en yüksek performans zirvesinde tutar
hakkında daha fazlası için Çin enjeksiyon kalıplama maliyeti,lütfen ziyaret edin https://www.jasonmolding.com/
Soruşturma İletişim:
İlgili kişi: James Yuan
Şirket Adı: JasonMould Sanayi Limited Şirketi
Adres: Uzun Çete Köyü,LongXi Kasabası,BoLuo İlçe,HuiZhou Şehri,Guangdong Eyaleti, Çin
Telefon: 86-752-6682869
E-posta: [email protected]
İnternet sitesi: https://www.jasonmolding.com