(1). MeetSthe requirements of working conditions
- Verschleißfestigkeit
Beim Rohling liegt Kunststoff im Formhohlraum, die Oberfläche des Hohlraums fließt und gleitet entlang der Oberfläche des Hohlraums, die die Reibung zwischen der Oberfläche der Kavität und dem Rohling verursacht, which causes the die to fail because of the wear. So the wear resistance of the material is one of the most basic and important properties of the mold.
Hardness is the main factor affecting the wear resistance. Im Allgemeinen, the higher the hardness of the die parts, the less the wear, the better the wear resistance. In Ergänzung, Die Verschleißfestigkeit ist auch typabhängig, Menge, Form, Größe und Verteilung der Karbide im Material.
2, strength and toughness
Die meisten Arbeitsbedingungen der Matrizen sind sehr schlecht, and some of them often bear a large impact load, was zu Sprödbruch führt. In order to prevent the sudden brittle fracture of die parts, the die must have high strength and toughness.
Die Zähigkeit der Matrize hängt hauptsächlich vom Kohlenstoffgehalt ab, Körnung
and microstructure of the material.
- Fatigue fracture properties
During the working process of dies, fatigue fracture often occurs under the long-term effect of cyclic stress. Its forms are low energy multiple impact fatigue fracture, tensile fatigue fracture contact fatigue fracture and bending fatigue fracture.
The fatigue fracture properties of the die mainly depend on its strength, Zähigkeit, Härte und der Gehalt an Einschlüssen im Material.
4, high temperature performance
When the working temperature of the die is higher, the hardness and strength of the die will decrease, resulting in early wear or plastic deformation of the die and failure. Because the mold material should have high tempering stability to ensure that the mold at the working temperature, with high hardness and strength. 5. Resistance to cold and hot fatigue
Some moulds are in the state of repeated heating and cooling in the working process, making the surface of the cavity under the action of tension and stress, Dies führt zu Rissen und Abblättern der Oberfläche, zunehmende Reibung, hindering the plastic deformation and reducing the size accuracy, resulting in the failure of the mold. Cold and hot fatigue is one of the main failure modes of hot working dies, die eine hohe Kälte- und Heißermüdungsbeständigkeit aufweisen sollten.
- Corrosion resistance
Some molds, such as plastic moulds in the work, because of the existence of chlorine, Fluor und andere Elemente im Kunststoff, decomposed and precipitated HCI, HF and other strong erosive gases after heating, eroding the mold cavity surface, increasing the surface roughness and aggravating the wear failure.
(2) Meets the requirements of the process performance
Mould manufacturing generally has to go through forging, Schneiden, heat treatment and other processes. In order to ensure the manufacturing quality of the mold and reduce the production cost, the material should have good Forgability, Bearbeitbarkeit, hardenability, hardenability and grinding property; it should also have small oxidation, decarburization
sensitivity and quenching dehiscence tendency.
- Forgability
It has low hot forging deformation resistance, good plasticity, wide forging temperature range, low tendency of cold cracking and precipitation of network carbide.
- Annealing process
The spheroidizing annealing temperature range is wide, the annealing hardness is low and the fluctuation range is small, and the spheroidizing rate is high.
3, Bearbeitbarkeit
Large cutting parameters, low tool loss, low surface roughness.
4, oxidation and decarburization sensitivity
When heated at high temperature, the oxidation resistance is good, the decarbonization rate is slow, and it is insensitive to the heating medium, so the tendency of pitting is small.
- Hardenability
Nach dem Abschrecken, it has uniform and high surface hardness.
6, hardenability
A deeper hardening layer can be obtained after quenching, and the hardening can be achieved by using a moderate quenching medium.
7, the tendency of quenching and dehiscence
The volume change of conventional quenching is small, the shape warpage and distortion are slight, and the tendency of abnormal deformation is low. Conventional quenching has low cracking sensitivity and is insensitive to quenching temperature and workpiece shape.
8, grindability
The relative loss of grinding wheel is small, the limit grinding amount without burn is large, and it is insensitive to the quality of grinding wheel and cooling condition, and is not easy to occur grinding damage and grinding cracks.
(3) Meets the economic requirement
In the selection of die materials, we must consider the principle of economy, as far as possible to reduce manufacturing costs. Deshalb, under the premise of satisfying the service performance, the first choice of low price, can use carbon steel without alloy steel, can use domestic materials without imported materials. In Ergänzung, the production and supply of the market should also be taken into account in the selection of materials, the selected steel should be as few and centralized as possible, easy to buy.
JasonMould Industrial Company Limited, etabliert in 2010, ist ein führender Spritzgusshersteller in China. JasonMould ist spezialisiert auf die Herstellung von Kunststoffformen für Haushaltsgeräte, medizinische Geräte, elektronische Geräte, Sicherheitseinrichtungen sowie Überwachungssystem.
Das Unternehmen hat über 15000 Quadratmeter Fabrik. Mit Geschäftsbereichen für Kunststoffspritzgusswerkzeuge mit unterschiedlichem Maschinenpark und Know-how, JasonMould bietet Werkzeuge von kleinen und präzisen Handyteilen bis hin zu so großen wie Automobilteilen. Unsere Werkzeuge werden hauptsächlich in die USA exportiert., Europa, Japan und Großbritannien. Die Diversifizierungsstrategie und der umfassende Service von JasonMould haben Kunden auf der ganzen Welt gelobt.
Unsere Mission ist es, unseren Kunden qualitativ hochwertige Spritzgussprodukte und Dienstleistungen anzubieten. Unser Ziel ist es, die Preiserwartungen unserer Kunden zu übertreffen, Qualität und pünktliche Lieferung. Um unsere Mission zu erfüllen, JasonMould:
- Verpflichtet sich, die Fähigkeiten und die Effizienz der Mitarbeiter kontinuierlich zu verbessern,
- Bietet unseren Mitarbeitern eine saubere und sichere Arbeitsumgebung,
- Aktualisiert Maschinentechnologie und unterstützende Ausrüstung durch ein strenges Wartungsprogramm, und
- Hält die Werkzeuge der Kunden auf höchstem Leistungsniveau
Für mehr über kundenspezifische Hersteller von Kunststoffformteilen,bitte besuche https://www.jasonmolding.com/
Anfrage Kontakt:
Gesprächspartner: James Yuan
Name der Firma: JasonMould Industrial Company Limited
Adresse: LongGang-Dorf,LongXi-Stadt,Bezirk BoLuo,Stadt HuiZhou,Provinz Guangdong, China
Telefon: 86-752-6682869
Email: [email protected]
Webseite: https://www.jasonmolding.com