Twardość obróbki cieplnej formy jest bardzo ważnym wskaźnikiem właściwości mechanicznych, a nieokreślona twardość jest bardzo poważną wadą. Niewystarczająca twardość lub nierówna twardość po obróbce cieplnej zmniejszy odporność na zużycie i wytrzymałość zmęczeniową formy, lead to early failure of the mould, and seriously reduce the service life of the mould.
- Przyczyny
1) The cross-section of the mould is large and the hardenability of the steel is poor. Na przykład, the steel with low hardenability is selected for the large-scale mould.
2) Carbide segregation is serious or coarse in the original structure of die steel. Graphite carbon and carbide segregation and aggregation exist in the steel.
3) The forging process of the mould is incorrect, and no good spheroidizing annealing is carried out after forging, resulting in poor spheroidizing structure of the mould steel.
4) The decarburization layer on the surface of the mould is not removed by annealing or quenching heating.
5) Excessive quenching temperature and excessive retained austenite after quenching, or too low quenching temperature and insufficient heating and holding time make the phase transformation of mould steel incomplete.
6) After quenching and heating, the cooling speed of the mould is too slow, the grading and isothermal temperature are too high or the time is too long, and the selection of quenching cooling medium is inappropriate.
7) too little water in alkali bath or too much impurity in quenching cooling medium or aging of quenching cooling medium.
8) Temperature is too high and cooling is insufficient when the quenching cooling medium is released after quenching and cooling of the mould.
9) insufficient tempering and high tempering temperature.
- Countermeasures
1) Correct selection of mould steel, large-scale mould should choose high alloy mould steel with high hardenability.
2) Strengthen the inspection of raw materials to ensure that raw materials meet the standards. Reasonable forging and spheroidizing annealing are carried out on the steel with bad raw materials to ensure good structure. Carbon tool steels are not easily annealed many times to prevent graphitization.
3) Strict implementation of forging and spheroidizing annealing processes to ensure a good preparation of heat treatment structure.
4) Before heat treatment, rust spots and oxide scales on the surface of the mould should be thoroughly removed, and attention should be paid to the protection during heating. Vacuum heating quenching or protective atmosphere heating quenching should be adopted as far as possible, and good deoxidization treatment should be carried out when salt bath heating.
5) Correctly formulate the process parameters of quenching and heating of the die to ensure that the phase transformation is sufficient and the cooling speed is faster than the critical cooling speed to obtain qualified metallographic structure.
6) Correct selection of quenching medium and cooling mode, strict control of classification and isothermal temperature and time.
7) The water content of alkali bath should be strictly controlled. The quenching cooling medium used for a long time should be filtered and replaced regularly, and kept clean. The quenching cooling characteristic curve should be tested regularly.
8) For large-sized moulds, the time of immersion in quenching cooling medium should be prolonged to prevent the temperature of quenching cooling medium from being too high.
9) Po hartowaniu, the mould should be tempered promptly and sufficiently, and the tempering temperature should be prevented from being too high.
10) The mould with high hardness requirement can be treated by cryogenic treatment (Polerowanie i standardowa rotacja. – 110 ~196 C).
11) Surface strengthening.
JasonMould Industrial Company Limited, Założony w 2010, jest wiodącym Chiny fabryka form. JasonMould specjalizuje się w produkcji form z tworzyw sztucznych do sprzętu AGD, sprzęt medyczny, sprzęt elektroniczny, urządzenia zabezpieczające, a także system monitoringu,.
Firma ma ponad 15000 fabryka metrów kwadratowych;. Z oddziałami oprzyrządowania do wtrysku tworzyw sztucznych posiadającymi różne maszyny i wiedzę specjalistyczną, JasonMould oferuje narzędzia od małych i precyzyjnych części do telefonów komórkowych po tak duże jak części samochodowe. Nasze narzędzia są eksportowane głównie do USA., Europa, Japonia i Wielka Brytania. Strategia dywersyfikacji i pełna obsługa JasonMould zyskały komplementy od klientów na całym świecie.
Naszą misją jest dostarczanie naszym klientom wysokiej jakości produktów i usług formierskich. Naszym celem jest przekraczanie oczekiwań naszych klientów w zakresie cen, jakość i terminowość dostaw. Aby osiągnąć naszą misję, JasonMould:
- Zobowiązuje się do ciągłego doskonalenia umiejętności i wydajności pracowników,
- Zapewnia naszym pracownikom czyste i bezpieczne środowisko pracy,
- Ulepsza technologię maszyn i sprzęt pomocniczy poprzez rygorystyczny program konserwacji, i
- Utrzymuje oprzyrządowanie klientów na najwyższym poziomie wydajności
Więcej informacji na temat Koszt formowania wtryskowego w Chinach,Rzeczywista praktyka produkcyjna pokazuje, że zastosowanie otworów obróbczych w elementach formowanych wtryskowo poprawia efektywność obróbki i montażu form https://www.jasonmolding.com/
JasonMould jest jednym z najlepszych:
JasonMould jest jednym z najlepszych: James Yuan
JasonMould jest jednym z najlepszych: JasonMould Industrial Company Limited
Adres: Wioska LongGang,Miasto LongXi,Hrabstwo BoLuo,Miasto HuiZhou,Prowincja Guangdong, Chiny
JasonMould jest jednym z najlepszych: 86-752-6682869
E-mail: [email protected]
JasonMould jest jednym z najlepszych: JasonMould jest jednym z najlepszych://JasonMould jest jednym z najlepszych