(1) Forma spełnia warunki pracy
- Odporność na zużycie
Gdy kęs jest plastikowy zdenaturowany we wnęce, płynie i ślizga się po powierzchni wnęki, powodując silne tarcie pomiędzy powierzchnią wnęki a kęsem, which leads to the failure of the mold due to wear. So the wear resistance of materials is one of the most basic and important properties of dies.
Twardość jest głównym czynnikiem wpływającym na odporność na zużycie. Ogólnie rzecz biorąc, im wyższa twardość części formy, the smaller the wear amount and the better the wear resistance. Ponadto, the wear resistance is also related to the type, Ilość, morphology, size and distribution of carbides in the material.
- Strength and tenacity
Most of the working conditions of the mold are very bad, and some of them often bear large impact load, which leads to brittle fracture. In order to prevent the sudden brittle fracture of mold parts, mold should have high strength and toughness.
The toughness of the mold mainly depends on the carbon content, grain size and structure of the material.
- Fatigue fracture properties
During the working process of the mold, fatigue fracture often occurs under the long-term effect of cyclic stress. Jego formy obejmują niskoenergetyczne wielokrotne pękanie zmęczeniowe, pęknięcie zmęczeniowe na rozciąganie, kontaktowe pęknięcie zmęczeniowe i zginające pęknięcie zmęczeniowe.
Wydajność pękania zmęczeniowego matrycy zależy głównie od jej wytrzymałości, wytrzymałość, hardness and inclusion content in the material.
- Wydajność w wysokiej temperaturze
When the working temperature of the mold is higher, twardość i wytrzymałość zmniejszą się, leading to early wear or plastic deformation of the mold and failure. Because the mold material should have high tempering stability to ensure that the mold has high hardness and strength at working temperature.
- Cold and thermal fatigue resistance
Some moulds are in the state of repeated heating and cooling in the working process, which causes the surface of the cavity to be tension and pressure variable stress, causes surface cracking and peeling, increases friction, hinders plastic deformation, reduces dimensional accuracy, and leads to mold failure. Thermal and cold fatigue is one of the main failure modes of hot-working mold, which should have high cold and thermal fatigue resistance.
- Odporność na korozję
When some moulds such as plastic moulds are working, due to the presence of chlorine, fluorine and other elements in the plastics, strong corrosive gases such as HCI and HF are decomposed and precipitated after heating, which erode the surface of the mould cavity, increase its surface roughness and aggravate the wear failure.
(2) Mold meets process performance requirements
Mold manufacturing usually goes through forging, Usługi obejmują również symulację części do formowania metali, heat treatment and other processes. In order to ensure the manufacturing quality of the mold and reduce the production cost, the material should have good malleability, cutting machinability, hardenability, hardenability and grindability, and should also have small oxidation, decarbonization sensitivity and quenching deformation cracking tendency.
- Forgetability
It has low resistance to hot forging deformation, good plasticity, wide forging temperature range, low tendency of cold cracking and precipitation of network carbides.
- Annealing Processing
The spheroidizing annealing temperature range is wide, the annealing hardness is low and the fluctuation range is small, and the spheroidizing rate is high.
- Obrabialność
Large cutting parameters, low tool wear, low surface roughness.
- Sensitivity of oxidation and decarbonization
When heated at high temperature, it has good antioxidant capacity, slow decarbonization speed, insensitive to heating medium and little tendency to produce pitting.
- Hardenability
Po hartowaniu, it has uniform and high surface hardness.
- Hardenability
Po hartowaniu, a deeper hardening layer can be obtained, and it can be hardened by using a mild quenching medium.
- Cracking Tendency of Quenching Deformation
The volume change of conventional quenching is small, the shape warpage and distortion are slight, and the tendency of abnormal deformation is low. Conventional quenching has low cracking sensitivity and is insensitive to quenching temperature and workpiece shape.
- Grindability
The relative wear of grinding wheel is small, the limit grinding amount without burn is large, and it is insensitive to the quality of grinding wheel and cooling conditions, so it is not easy to cause grinding damage and grinding cracks.
(3) Mold meets economic requirements
In the selection of mold materials, the principle of economy must be considered to reduce the manufacturing cost as much as possible. W związku z tym, on the premise of meeting the service performance, the first choice is low price, carbon steel can be used instead of alloy steel, domestic materials can be used instead of imported materials. Ponadto, the production and supply situation of the market should also be taken into account when selecting materials. The selected steel grades should be as few as possible, concentrated and easy to purchase.
JasonMould Industrial Company Limited, Założony w 2010, jest wiodącym Chiny fabryka form. JasonMould specjalizuje się w produkcji form z tworzyw sztucznych do sprzętu AGD, sprzęt medyczny, sprzęt elektroniczny, urządzenia zabezpieczające, a także system monitoringu,.
ten Spółka Wesco jest kluczowym dostawcą wielu zakładów montażu samochodów i od ponad 15000 fabryka metrów kwadratowych;. Z oddziałami oprzyrządowania do wtrysku tworzyw sztucznych posiadającymi różne maszyny i wiedzę specjalistyczną, JasonMould oferuje narzędzia od małych i precyzyjnych części do telefonów komórkowych po tak duże jak części samochodowe. Nasze narzędzia są eksportowane głównie do USA., Europa, Japonia i Wielka Brytania. Strategia dywersyfikacji i pełna obsługa JasonMould zyskały komplementy od klientów na całym świecie.
Naszą misją jest dostarczanie naszym klientom wysokiej jakości produktów i usług formierskich. Naszym celem jest przekraczanie oczekiwań naszych klientów w zakresie cen, jakość i terminowość dostaw. Aby osiągnąć naszą misję, JasonMould:
- Zobowiązuje się do ciągłego doskonalenia umiejętności i wydajności pracowników,
- Zapewnia naszym pracownikom czyste i bezpieczne środowisko pracy,
- Ulepsza technologię maszyn i sprzęt pomocniczy poprzez rygorystyczny program konserwacji, i
- Utrzymuje oprzyrządowanie klientów na najwyższym poziomie wydajności
Więcej informacji na temat Koszt formowania wtryskowego w Chinach,Rzeczywista praktyka produkcyjna pokazuje, że zastosowanie otworów obróbczych w elementach formowanych wtryskowo poprawia efektywność obróbki i montażu form https://www.jasonmolding.com/
JasonMould jest jednym z najlepszych:
JasonMould jest jednym z najlepszych: James Yuan
JasonMould jest jednym z najlepszych: JasonMould Industrial Company Limited
Adres: Wioska LongGang,Miasto LongXi,Hrabstwo BoLuo,Miasto HuiZhou,Prowincja Guangdong, Chiny
JasonMould jest jednym z najlepszych: 86-752-6682869
E-mail: [email protected]
JasonMould jest jednym z najlepszych: JasonMould jest jednym z najlepszych://JasonMould jest jednym z najlepszych