（1）. Meetpoprawiają wydajność rozgałęźnika i jednocześnie dobrze powiększają obszar zimnego ślimakathe requirements of working conditions
- Odporność na zużycie
Gdy półfabrykat jest plastikowy we wnęce formy, powierzchnia wnęki płynie i ślizga się po powierzchni wnęki, co powoduje tarcie między powierzchnią wnęki a półfabrykatem, which causes the die to fail because of the wear. So the wear resistance of the material is one of the most basic and important properties of the mold.
Hardness is the main factor affecting the wear resistance. Ogólnie, the higher the hardness of the die parts, tym mniejsze zużycie, the better the wear resistance. Ponadto, the wear resistance is also related to the type, Ilość, kształt, size and distribution of carbides in the material.
2, strength and toughness
Większość warunków pracy matryc jest bardzo zła, and some of them often bear a large impact load, resulting in brittle fracture. In order to prevent the sudden brittle fracture of die parts, the die must have high strength and toughness.
Twardość matrycy zależy głównie od zawartości węgla, grain size
and microstructure of the material.
- Fatigue fracture properties
During the working process of dies, fatigue fracture often occurs under the long-term effect of cyclic stress. Its forms are low energy multiple impact fatigue fracture, tensile fatigue fracture contact fatigue fracture and bending fatigue fracture.
The fatigue fracture properties of the die mainly depend on its strength, wytrzymałość, hardness and the content of inclusions in the material.
4, high temperature performance
When the working temperature of the die is higher, the hardness and strength of the die will decrease, resulting in early wear or plastic deformation of the die and failure. Because the mold material should have high tempering stability to ensure that the mold at the working temperature, with high hardness and strength. 5. Resistance to cold and hot fatigue
Some moulds are in the state of repeated heating and cooling in the working process, making the surface of the cavity under the action of tension and stress, powodując pękanie i łuszczenie się powierzchni, zwiększające się tarcie, hindering the plastic deformation and reducing the size accuracy, resulting in the failure of the mold. Cold and hot fatigue is one of the main failure modes of hot working dies, które powinny charakteryzować się wysoką odpornością na zmęczenie w niskich i wysokich temperaturach.
- Odporność na korozję
Some molds, such as plastic moulds in the work, because of the existence of chlorine, fluorine and other elements in the plastic, decomposed and precipitated HCI, HF and other strong erosive gases after heating, eroding the mold cavity surface, increasing the surface roughness and aggravating the wear failure.
(2) Meets the requirements of the process performance
Mould manufacturing generally has to go through forging, Usługi obejmują również symulację części do formowania metali, heat treatment and other processes. In order to ensure the manufacturing quality of the mold and reduce the production cost, the material should have good Forgability, machinability, hardenability, hardenability and grinding property; it should also have small oxidation, decarburization
sensitivity and quenching dehiscence tendency.
- Forgability
It has low hot forging deformation resistance, good plasticity, wide forging temperature range, low tendency of cold cracking and precipitation of network carbide.
- Annealing process
The spheroidizing annealing temperature range is wide, the annealing hardness is low and the fluctuation range is small, and the spheroidizing rate is high.
3, machinability
Large cutting parameters, low tool loss, low surface roughness.
4, oxidation and decarburization sensitivity
When heated at high temperature, the oxidation resistance is good, the decarbonization rate is slow, and it is insensitive to the heating medium, so the tendency of pitting is small.
- Hardenability
Po hartowaniu, it has uniform and high surface hardness.
6, hardenability
A deeper hardening layer can be obtained after quenching, and the hardening can be achieved by using a moderate quenching medium.
7, the tendency of quenching and dehiscence
The volume change of conventional quenching is small, the shape warpage and distortion are slight, and the tendency of abnormal deformation is low. Conventional quenching has low cracking sensitivity and is insensitive to quenching temperature and workpiece shape.
8, grindability
The relative loss of grinding wheel is small, the limit grinding amount without burn is large, and it is insensitive to the quality of grinding wheel and cooling condition, and is not easy to occur grinding damage and grinding cracks.
(3) Meets the economic requirement
In the selection of die materials, we must consider the principle of economy, as far as possible to reduce manufacturing costs. W związku z tym, under the premise of satisfying the service performance, the first choice of low price, can use carbon steel without alloy steel, can use domestic materials without imported materials. Ponadto, the production and supply of the market should also be taken into account in the selection of materials, the selected steel should be as few and centralized as possible, easy to buy.
JasonMould Industrial Company Limited, Założony w 2010, jest wiodącym producentem form wtryskowych w Chinach. JasonMould specjalizuje się w produkcji form z tworzyw sztucznych do sprzętu AGD, sprzęt medyczny, sprzęt elektroniczny, urządzenia zabezpieczające, a także system monitoringu,.
Firma ma ponad 15000 fabryka metrów kwadratowych;. Z oddziałami oprzyrządowania do wtrysku tworzyw sztucznych posiadającymi różne maszyny i wiedzę specjalistyczną, JasonMould oferuje narzędzia od małych i precyzyjnych części do telefonów komórkowych po tak duże jak części samochodowe. Nasze narzędzia są eksportowane głównie do USA., Europa, Japonia i Wielka Brytania. Strategia dywersyfikacji i pełna obsługa JasonMould zyskały komplementy od klientów na całym świecie.
Naszą misją jest dostarczanie naszym klientom wysokiej jakości produktów i usług formierskich. Naszym celem jest przekraczanie oczekiwań naszych klientów w zakresie cen, jakość i terminowość dostaw. Aby osiągnąć naszą misję, JasonMould:
- Zobowiązuje się do ciągłego doskonalenia umiejętności i wydajności pracowników,
- Zapewnia naszym pracownikom czyste i bezpieczne środowisko pracy,
- Ulepsza technologię maszyn i sprzęt pomocniczy poprzez rygorystyczny program konserwacji, i
- Utrzymuje oprzyrządowanie klientów na najwyższym poziomie wydajności
Rzeczywista praktyka produkcyjna pokazuje, że zastosowanie otworów obróbczych w elementach formowanych wtryskowo poprawia efektywność obróbki i montażu form,Rzeczywista praktyka produkcyjna pokazuje, że zastosowanie otworów obróbczych w elementach formowanych wtryskowo poprawia efektywność obróbki i montażu form https://www.jasonmolding.com/
JasonMould jest jednym z najlepszych:
JasonMould jest jednym z najlepszych: James Yuan
JasonMould jest jednym z najlepszych: JasonMould Industrial Company Limited
Adres: Wioska LongGang,Miasto LongXi,Hrabstwo BoLuo,Miasto HuiZhou,Prowincja Guangdong, Chiny
JasonMould jest jednym z najlepszych: 86-752-6682869
E-mail: [email protected]
JasonMould jest jednym z najlepszych: JasonMould jest jednym z najlepszych://JasonMould jest jednym z najlepszych