ПК-пластики обладают превосходными свойствами., высокая прозрачность, хорошая ударная вязкость, сопротивление ползучести, широкий диапазон температур. Поликарбонатные пластмассы имеют следующие технологические характеристики
Чувствительность вязкости расплава к скорости сдвига мала, но до температуры большая, нет очевидной точки плавления, the viscosity of melt is high, the resin is easy to hydrolyze at high temperature, and the product is easy to crack. In view of these characteristics, special attention should be paid to differential treatment: повысить текучесть расплава, it is not achieved by increasing the injection pressure but by increasing the injection temperature. The runner and gate of the mould are required to be short and thick, so as to reduce the pressure loss of the fluid and have a higher injection pressure. The resin shall be fully dried before forming and processing to control its moisture content below 0.02%. Кроме того, insulation measures shall be taken for the resin during processing to prevent moisture absorption again. It is not only necessary to design the products reasonably, but also to master the forming process correctly, such as increasing the mold temperature, post-treatment of the products and so on, which can reduce or eliminate the internal stress. Adjust the process parameters in time according to the different conditions of the products.
Process characteristics of PC: PC viscosity is large, melt temperature is high, and fluidity is poor. В таком случае, it must be injection molded at a higher temperature (270 ~ 320 ℃), relatively narrow range of material temperature adjustment, and the processibility is inferior to PMMA. The injection pressure has little effect on the fluidity, but because of the high viscosity, the injection pressure still needs to be higher. Чтобы предотвратить внутреннее напряжение, время выдержки давления должно быть как можно короче. Степень усадки большая, а размер стабильный., но внутреннее напряжение изделия велико и его легко расколоть, so it is better to improve the fluidity by increasing the temperature rather than the pressure, and reduce the possibility of cracking by increasing the temperature of the mold, improving the structure of the mold and post-treatment. Когда скорость впрыска низкая, the gate is easy to produce corrugations and other defects. Температура радиального сопла должна контролироваться отдельно., температура формы должна быть высокой, и сопротивление бегунка и ворот должно быть небольшим.
Injection molding performance of PC: PC is a crystalline plastic with obvious melting point. It melts at 220 ℃ and decomposes at 350 ℃; the general processing temperature is 250-320 ℃; it absorbs water and a small amount of water can cause it to decompose at high temperature. Во время литья под давлением, it must be dried, and the drying temperature can be used at 120 ℃ for 4-5h; the melting viscosity of PC material is large, so it needs a large pressure during injection molding; In the processing of PC plastics, if the conditions permit, the mold temperature can be increased by the mold temperature machine to reduce the residual stress of the product; if the product has inserts, the diameter of the inserts is less than 1-2mm, preheating can be ignored, and the larger inserts should be considered preheating, иначе, stress cracking will occur; The shrinkage of PC has nothing to do with the processing conditions and the wall thickness of the products. Its longitudinal and transverse shrinkage are relatively close, so it can be processed into products with high precision. Its shrinkage is 5 ‰ and the overflow value is 0.05mm.
(1) Температура впрыска
It can only be made after considering the shape, размер, структура формы, product performance, requirements and other aspects of the product. Обычно, when the temperature is between 270 ℃ и 320 ℃, if the material temperature is higher than 340 ℃, PC will decompose, the color of products will become darker, and defects such as silver wire, dark strip, черное пятно, bubble will appear on the surface, and the physical and mechanical properties will also decline significantly.
(2) включая требования к литьевой машине
It has a certain influence on the physical and mechanical properties, внутреннее напряжение, molding shrinkage of PC plastic products, and has a great influence on the appearance and demoulding performance of products. Too low or too high injection pressure will cause some defects of products. Обычно, the injection pressure is controlled between 80 ~ 120MPa for thin-walled, long process, complex shape and small gate products, in order to overcome the melt flow Resistance, so that even if the mold cavity is full, a higher injection pressure (120-145МПа) can be selected to obtain a complete and smooth surface of the product.
(3) Pressure maintaining pressure and time
The magnitude and duration of holding pressure have great influence on the internal stress of PC products. Too small holding pressure, small feeding effect, easy to appear vacuum bubble or surface shrinkage; too large holding pressure, easy to produce large internal stress around the gate. In actual processing, the method of high material temperature and low holding pressure is often used to solve this problem. The selection of holding time depends on the thickness of products, и с некоторыми ненадежными нагревательными и проводящими принадлежностями, температура пресс-формы, так далее. в целом, small and thin products do not need a long holding time; on the contrary, large and thick products should have a long holding time. The length of holding time can be determined by the test of gate sealing time.
(4) включая требования к литьевой машине
There is no obvious effect on the performance of PC products. Except for thin-walled, small gate, deep hole and long process products, medium speed or slow processing is generally adopted, multi-level injection is preferred, and slow fast slow multi-level injection is generally adopted.
(5) должен быть как можно короче
Обычно, it can be controlled at 80-100 ℃, and it can also be increased to 100-120 ℃ for products with complex shape, thinner and higher requirements, but it can not exceed the hot deformation temperature of the mold.
(6) должен быть как можно короче
Due to the high viscosity of PC melt, the requirement of screw speed should not be too high to prevent the screw from being overloaded, which is favorable for the maintenance of plasticizing, exhausting and injection molding machine. It is generally suitable to control the screw speed at 30 ~ 60R / мин, while the back pressure should be controlled at 10% ~ 15% давления впрыска.
(7) release agent
В процессе литья под давлением, the use of release agent should be strictly controlled, and the use of recycled material should not exceed three times, and the use amount should be about 20%.
(8) It is required that the maximum injection volume (including flow channel, gate, и т.п.) of PC products should be no more than 70% ~ 80% of the nominal injection volume
The length diameter ratio (L / D) of the screw is 15 ~ 20, and the set compression ratio is 15 ~ 20
О компании JasonMould Industrial Company Limited
Джейсонмулд - это Производитель пресс-форм в Китае пластиковых форм- пресс-форма для литья под давлением, формы для литья под давлением, выдувное формование пластика, ротационное формование, медицинский литье пластмасс под давлением, два выстрела литье пластмасс под давлением, вставка молдинга, формование, литье металла под давлением, микро литье под давлением, порошковое литье под давлением, керамическое литье под давлением, жидкое литье под давлением, хаски литье под давлением, бытовая плесень, литейная форма, инструмент для штамповки, нестандартные формы, фарфоровые формы, инструменты для быстрого прототипирования, инструменты для изготовления пластиковых прототипов, инструмент для штамповки, штамп и инструменты для деталей мобильных / сотовых телефонов, автомобильные запчасти, пылесосы, аккумуляторные инструменты, телефоны, копировальные аппараты, компьютеры, мультимедийные колонки, и многие другие электронные товары и бытовая техника. А также производитель пластиковых изделий, производитель пресс-форм Китай- пластиковые детали, пластиковый резервуар для воды, пластиковые шары, пластиковые контейнеры, пластиковая пряжка, пластиковый якорь, пластиковая вешалка, пластиковая ложка, пластиковые фитинги, пластиковая мешалка, пластиковая посуда, пластиковые стаканы, пластиковые бутылки, пластиковый поднос, пластиковый косметический контейнер, пластиковый корпус, пластиковый контейнер для еды, пластиковые стулья, пластиковые колпачки, пластиковая крышка, пластиковые трубки, пластиковые водопроводные трубы, пластиковые ручки, пластиковые трубки, пластиковые хозяйственные ящики, пластиковые стойки и тд.
Контакт:
Человек: Джеймс Юань
Компания: JasonMould Industrial Company Limited
Добавлять: Деревня ЛонгГанг,LongXi Town,Округ БоЛуо,Город Хуэйчжоу,Провинция Гуандонг, Китай
Тел.: 86-752-6682869
Электронное письмо: [email protected]
Сайт: https://www.jasonmolding.com/custom-injection-molding/