1. 강도 성능
(1) 경도
경도는 금형강의 주요 기술 지표입니다.. 높은 응력의 작용에서 모양과 크기를 변하지 않게 유지하기 위해, 다이는 충분히 높은 경도를 가져야 합니다.. The hardness of cold working mold steel is generally maintained at about HRC60 at room temperature. According to its working conditions, hot working mold steel is generally required to be maintained in the range of hrc40 ~ 55.
For the same steel, within a certain range of hardness value, the hardness is directly proportional to the deformation resistance; 하나, there may be obvious differences in plastic deformation resistance between steel grades with the same hardness value and different composition and structure.
(2) Red hardness
The hot working mold working at high temperature is required to maintain the stability of its structure and performance, so as to maintain high enough hardness. This performance is called red hardness.
Carbon tool steel and low alloy tool steel can usually maintain this property in the temperature range of 180 ~ 250 ℃, and chromium molybdenum hot working die steel can generally maintain this property in the temperature range of 550 ~ 600 ℃. The red hardness of steel mainly depends on the chemical composition and heat treatment process of steel.
(3) Compressive yield strength and compressive bending strength
The mold is often subjected to high strength pressure and bending in the process of use, so the mold material is required to have certain compressive strength and flexural strength.
많은 경우에, the conditions of compression test and bending test are close to the actual working conditions of the mold (예를 들어, the measured compressive yield strength of die steel is consistent with the deformation resistance of the punch during operation).
Another advantage of bending test is that the value of strain is large, which can sensitively reflect the difference of deformation resistance between different steel grades and under different heat treatment and microstructure.
2. Tenacity
In the working process, the die bears the impact load. In order to reduce the damage in the form of breaking and edge collapse in the process of use, the die steel is required to have a certain toughness.
The chemical composition, 입자 크기, purity, 수량, 형태, size and distribution of carbides and inclusions, as well as the heat treatment system and metallographic structure of die steel have a great impact on the toughness of steel. 특히, the purity and hot working deformation of steel have more obvious effects on its transverse toughness.
The toughness, strength and wear resistance of steel are often contradictory. 따라서, it is necessary to reasonably select the chemical composition of steel and adopt reasonable refining, hot working and heat treatment processes, so as to make the wear resistance, strength and toughness of die materials achieve a good combination.
Impact toughness is the total energy absorbed by the specimen in the whole fracture process during one impact. 하나, many tools are fatigue fracture under different working conditions. 따라서, the conventional impact toughness can not fully reflect the fracture performance of mold steel. Small energy multiple impact fracture work or multiple fracture life and fatigue life are being used.
3. 내마모성
The wear resistance of mold materials is often an important factor in determining the service life of dies. The die bears considerable compressive stress and friction in work, which requires the die to maintain its dimensional accuracy under strong friction. The wear of die is mainly mechanical wear, oxidation wear and melting wear.
In order to improve the wear resistance of die steel, it is necessary to not only maintain the high hardness of mold steel, but also ensure that the composition, morphology and distribution of carbides or other hardened phases in the steel are reasonable.
For the mold in service under the condition of heavy load and high-speed wear, it is required that the die steel surface can form a thin and dense oxide film with good adhesion, maintain the lubrication, reduce the molten wear such as bonding and welding between the die and the workpiece, and reduce the oxidation wear caused by oxidation on the die surface. 따라서, the working conditions of the die have a great influence on the wear of steel.
The wear resistance can be measured by the simulation test method, and the relative wear resistance index can be used as the parameter to characterize the wear resistance level under different chemical composition and organizational state. To present the service life before the specified burr height and reflect the wear resistance level of various steel grades; The test is based on Cr12MoV steel.
4. Thermal fatigue resistance
Under the service condition, hot work mold steel is not only subjected to the periodic change of load, but also subjected to the action of high temperature and periodic quenching and heating. 따라서, the evaluation of the fracture resistance of hot work die steel should pay attention to the thermomechanical fatigue fracture performance of materials. Thermomechanical fatigue is an index of comprehensive performance, which includes thermal fatigue performance, mechanical fatigue crack growth rate and fracture toughness.
Thermal fatigue performance reflects the working life of materials before thermal fatigue crack initiation. Materials with high thermal fatigue resistance have more thermal cycles for thermal fatigue crack initiation; The mechanical fatigue crack growth rate reflects the growth amount of each stress cycle when the crack propagates internally under the action of forging pressure after the thermal fatigue crack initiation; Fracture toughness reflects the resistance of materials to the unstable propagation of existing cracks.
For the material with high fracture toughness, if the crack wants to propagate unsteadily, it must have a sufficiently high stress intensity factor at the crack tip, 그건, it must have a large crack length. On the premise of constant stress, there is already a fatigue crack in a die. If the fracture toughness of the die material is high, the crack must expand deeper before instability propagation can occur.
품질에 영향을 미치기 쉽습니다, the thermal fatigue resistance determines the part of life before fatigue crack initiation; The crack growth rate and fracture toughness can determine the part of life where subcritical propagation occurs after crack initiation. 따라서, in order to obtain high service life of hot working die, the die material should have high thermal fatigue resistance, low crack growth rate and high fracture toughness.
The index of thermal fatigue resistance can be measured by the number of thermal cycles of thermal fatigue crack initiation, or by the number of fatigue cracks and average depth or length after a certain thermal cycle.
5. Occlusal resistance
Occlusal resistance is actually the resistance when “cold welding” occurs. This property is important for die materials.
During the test, under the condition of dry friction, the tested tool steel sample and the material with bite tendency (such as austenitic steel) are subjected to constant speed dual friction movement, and the load is gradually increased at a certain speed. 이때, the torque is also increased accordingly. This load is called “bite critical load”. The higher the critical load is, the stronger the bite resistance is.
사출 금형의 구조에서주의해야 할 세 가지 점은 전체 금형 배아와 금형 코어의 조정입니다., 주식회사
디제이 몰드는 중국 금형 제작자 플라스틱 금형- 사출 금형, 다이 캐스팅 금형, 플라스틱 블로우 성형, 회전 성형, 의료 플라스틱 사출 성형, 투샷 플라스틱 사출 성형, 인서트 몰딩, 오버 몰딩, 금속 사출 성형, 마이크로 사출 성형, 분말 사출 성형, 세라믹 사출 성형, 액체 사출 성형, 허스키 사출 성형, 가정용 곰팡이, 주조 금형, 금형 도구 다이, 맞춤 금형, 중국 금형, 신속한 프로토 타이핑 도구, 플라스틱 프로토 타이핑 툴링, 펀치 프레스 툴링, 모바일 / 휴대폰 부품 용 다이 및 툴링, 자동차 부품, 진공 청소기, 충전식 도구, 전화기, 복사기, 컴퓨터, 멀티미디어 스피커, 및 기타 많은 전자 제품 및 가전 제품. 또한 플라스틱 제품 제조업체, 금형 제조업체 중국– 플라스틱 부품, 플라스틱 물 탱크, 플라스틱 공, 플라스틱 용기, 플라스틱 버클, 플라스틱 앵커, 플라스틱 걸이, 플라스틱 숟가락, 플라스틱 파이프 피팅, 플라스틱 텀블, 플라스틱 식기, 플라스틱 컵들, 플라스틱 병, 플라스틱 쟁반, 플라스틱 화장품 용기, 플라스틱 케이스, 플라스틱 식품 용기, 플라스틱 의자, 플라스틱 캡, 플라스틱 캡 폐쇄, 플라스틱 튜브, 플라스틱 수도관, 플라스틱 손잡이, 플라스틱 튜브, 플라스틱 유틸리티 박스, 플라스틱 선반 등.
접촉:
사람: 제임스 위안
회사: 사출 금형의 구조에서주의해야 할 세 가지 점은 전체 금형 배아와 금형 코어의 조정입니다.
더하다: 롱강 빌리지,LongXi 타운,BoLuo 카운티,혜주시,광동성, 중국
Tel: 86-752-6682869
이메일: [email protected]