빌렛이 금형 캐비티에서 소성 변성 된 경우, 그것은 금형 캐비티의 외부 표면을 따라 움직이고 미끄러집니다., 이는 금형 캐비티의 외부 표면과 블랭크 사이에 심각한 충돌을 일으킵니다., and then leads to the failure of the mold due to wear and tear. So the wear resistance of materials is one of the most basic and important functions of the mold.
Hardness is the primary factor affecting wear resistance. 일반적으로 말하면, 금형 부품의 경도가 높을수록, 마모량이 적고 내마모성이 우수합니다.. 게다가, 내마모성은 유형과도 관련이 있습니다., 수량, 모양, size and distribution of carbides in the guess.
Second point: strong patience
Most of the working conditions of the molds are very bad, some of them often bear a large impact load, and then lead to brittle cracking. In order to avoid the sudden brittle fracture of mold parts in operation, the mold should have high strength and endurance.
The durability of the mold depends primarily on the carbon content, 재료의 입자 크기와 구조.
Third point: fatigue cracking function
In the process of mold operation, fatigue cracking often occurs under the action of cyclic stress for a long time. Its ways are small energy repeated impact fatigue cracking, tension fatigue cracking, touch fatigue cracking and tortuous fatigue cracking.
The fatigue cracking function of the mold mainly depends on its strength, endurance, hardness and inclusion content.
Fourth point: high temperature function
금형의 작동 온도가 높을 때, 경도와 강도가 감소합니다, leading to wear or plastic deformation in the early stage of the mold and failure. Because the mold data should have high temper resistance stability to ensure that the mold has high hardness and strength at operating temperature.
Fifth point: cold and heat exhaustion resistance function
Some molds are in the state of repeated heating and cooling in the process of operation, which makes the outer surface of the cavity subject to tension and pressure variable stress, causes cracking and shedding of the outer surface, increases the conflict force, prevents plastic deformation, reduces the scale accuracy, and then leads to mold failure. Hot and cold fatigue is one of the most important ways of failure of hot working dies. It is necessary for such molds to have high cold and heat fatigue resistance.
Sixth point: 내식성
Some molds such as plastic molds in operation, because there are chlorine, fluorine and other elements in the plastic guess, decompose into strong corrosive gases such as hci, HF after heating, corrode the appearance of the mold cavity, increase its surface roughness, and aggravate wear failure.
JasonMould 산업 회사 제한, 설립 2010, 선두이다 중국 금형 공장. JasonMould는 가전 제품을위한 플라스틱 금형 생산을 전문으로합니다., 의료 장비, 전자 장비, 안전 장비 및 모니터링 시스템.
회사는 끝났다 15000 평방 미터 공장. 다양한 기계 및 전문 지식을 보유한 플라스틱 사출 공구 부문, JasonMould는 작고 정밀한 휴대폰 부품에서 자동차 부품만큼 큰 도구를 제공합니다.. 우리의 도구는 주로 미국으로 수출됩니다., 유럽, 일본과 영국. JasonMould의 다각화 전략과 풀 서비스는 전 세계 고객들로부터 찬사를 받았습니다..
우리의 임무는 고객에게 고품질의 성형 제품과 서비스를 제공하는 것입니다.. 우리는 가격에 대한 고객의 기대치를 초과하는 것을 목표로합니다., 품질 및 정시 납품. 우리의 사명을 달성하기 위해, JasonMould:
- 직원의 기술과 효율성을 지속적으로 개선하기 위해 노력합니다.,
- 직원들에게 깨끗하고 안전한 작업 환경을 제공합니다.,
- 엄격한 유지 보수 프로그램을 통해 기계 기술 및 지원 장비를 업그레이드합니다., 과
- 고객의 툴링을 최고 성능으로 유지
에 대해 더 알아보기 중국 사출 성형 비용,방문하시기 바랍니다 https://www.jasonmolding.com/
문의처:
담당자: 제임스 위안
회사 이름: JasonMould 산업 회사 제한
주소: 롱강 빌리지,LongXi 타운,BoLuo 카운티,혜주시,광동성, 중국
전화: 86-752-6682869
이메일: [email protected]