사출 금형 가공 제품의 공정에서, Rapid Prototype은 다양한 분야에서 다양한 이유로 필요하며, 따라서 Rapid Prototyping 서비스는 글로벌 고객의 요구 사항을 충족하는 데 매우 중요합니다., Rapid Prototype은 다양한 분야에서 다양한 이유로 필요하며, 따라서 Rapid Prototyping 서비스는 글로벌 고객의 요구 사항을 충족하는 데 매우 중요합니다.. Rapid Prototype은 다양한 분야에서 다양한 이유로 필요하며, 따라서 Rapid Prototyping 서비스는 글로벌 고객의 요구 사항을 충족하는 데 매우 중요합니다..
Rapid Prototype은 다양한 분야에서 다양한 이유로 필요하며, 따라서 Rapid Prototyping 서비스는 글로벌 고객의 요구 사항을 충족하는 데 매우 중요합니다.
PA6 material is widely used in structural parts and has good wear resistance. Because of its low melting point, the process temperature range is very wide. Its impact resistance, solubility resistance and hygroscopicity are better than PA66.
Under the injection molding process conditions, PA6 needs to be dried, so special attention should be paid to the drying before processing. If the material is suitable for waterproof products, it is necessary to keep closed management. If the humidity is higher than 0.2%, it is recommended to dry above 80 ℃ for 16h. If the material has been exposed to air for more than 8h, vacuum drying at 105 ℃ for more than 8h is recommended.
Injection mold workshop
In the production of PA6 materials, attention should be paid to the mold temperature of injection mold processing: because the mold temperature can obviously affect the crystallinity, which in turn affects the characteristics of the product, the crystallinity is very important for structural parts, so it is recommended that the mold temperature be 80 ~ 90 ℃. For thin-walled products with long process, higher die temperature is recommended. Increasing the mold temperature can improve the strength of the product, but it will reduce the toughness. If the wall thickness is greater than 3mm, it is recommended to use 20 ~ 40 ℃ low temperature die. For glass fiber reinforced materials, the mold temperature should be higher than 80 ℃.
Injection mold_ Gate treatment
Injection mold processing mold runner and gate: because PA6 solidification time is very short, so the gate position is very important. The gate diameter should not be less than 0.5T. If hot runner is used, the gate size should be smaller than that of conventional runner, because hot runner can help prevent premature solidification of material. If submerged gate is used, the minimum diameter of gate should be 0.75mm.
From the above point of view, the injection mold processing products, each material has different characteristics, we combine all aspects of the conditions in the injection molding process to produce, in order to produce products that meet the requirements. If you want to know more about technology, you can log in to the official website ofJasonMould. There are detailed technical encyclopedias for your reference. We are looking forward to your visit!
JasonMould Industrial Company Limited 정보
Jasonmould는 중국 금형 제작자 플라스틱 금형- 사출 금형, 다이 캐스팅 금형, 플라스틱 블로우 성형, 회전 성형, 의료 플라스틱 사출 성형, 투샷 플라스틱 사출 성형, 인서트 몰딩, 오버 몰딩, 금속 사출 성형, 마이크로 사출 성형, 분말 사출 성형, 세라믹 사출 성형, 액체 사출 성형, 허스키 사출 성형, 가정용 곰팡이, 주조 금형, 금형 도구 다이, 맞춤 금형, 중국 금형, 신속한 프로토 타이핑 도구, 플라스틱 프로토 타이핑 툴링, 펀치 프레스 툴링, 모바일 / 휴대폰 부품 용 다이 및 툴링, 자동차 부품, 진공 청소기, 충전식 도구, 전화기, 복사기, 컴퓨터, 멀티미디어 스피커, 및 기타 많은 전자 제품 및 가전 제품. 또한 플라스틱 제품 제조업체, 금형 제조업체 중국– 플라스틱 부품, 플라스틱 물 탱크, 플라스틱 공, 플라스틱 용기, 플라스틱 버클, 플라스틱 앵커, 플라스틱 걸이, 플라스틱 숟가락, 플라스틱 파이프 피팅, 플라스틱 텀블, 플라스틱 식기, 플라스틱 컵들, 플라스틱 병, 플라스틱 쟁반, 플라스틱 화장품 용기, 플라스틱 케이스, 플라스틱 식품 용기, 플라스틱 의자, 플라스틱 캡, 플라스틱 캡 폐쇄, 플라스틱 튜브, 플라스틱 수도관, 플라스틱 손잡이, 플라스틱 튜브, 플라스틱 유틸리티 박스, 플라스틱 선반 등.
접촉:
사람: 제임스 위안
회사: JasonMould 산업 회사 제한
더하다: 롱강 빌리지,LongXi 타운,BoLuo 카운티,혜주시,광동성, 중국
Tel: 86-752-6682869
이메일: [email protected]